Arkema Group Orgalloy® LE 60 ES Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE 60 ES Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.86 % | 1.86 % | 23°C / 50% RH; ISO 62 |
| 6.4 % | 6.4 % | in 23°C water; ISO 62 | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 235 °C |
0.90 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ISO R527 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO R527 |
| Elongation at Break | 280 % | 280 % | ISO R527 |
| Elongation at Yield | 4.2 % | 4.2 % | ISO R527 |
| Modulus of Elasticity | 1.25 GPa | 181 ksi | ISO R527 |
| Flexural Strength | 40.0 MPa | 5800 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.800 GPa | 116 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 1.30 GPa | 189 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 2.20 J/cm² @Temperature -20.0 °C |
10.5 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 1.11 MPa | 161 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Vicat Softening Point | 97.0 °C | 207 °F | 50 N - B method; ISO 306 |
| 204 °C | 399 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Osprey Metals 317L Stainless Steel Powder (Grade 90% - 22)
- Precision Polymer Engineering F60R Fluorosilicone Rubber
- SABIC Innovative Plastics Lexan® SLX2432D PC Copolymer (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 19-7221/OR Polyamide 46, with glass fiber
- Huntsman DY 062 Epoxy Accelerator
- LyondellBasell Plexar® PX5335 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- Kolon DIAMAT® EM
- A. Schulman POLYBATCH™ Lattice Green 30155U Concentrate Based In LLDPE
- Axiall 5055 Rigid PVC, Extrusion, Natural
- Victrex® PEEK 150GL30 Black Polyetheretherketone, 30% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved