Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 5.00 - 6.00 GPa | 725 - 870 ksi | Injection; ISO 527 |
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi.. |
|||
Modulus of Elasticity | 5.00 - 7.00 GPa | 725 - 1020 ksi | Injection; ISO 527 |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Modulus of Elasticity | 5.00 - 7.00 GPa | 725 - 1020 ksi | Injection; ISO 527 |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Modulus of Elasticity | 5.00 - 7.00 GPa | 725 - 1020 ksi | Compression; ISO 527 |
Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
Modulus of Elasticity | 5.00 - 8.00 GPa | 725 - 1160 ksi | Injection and Compression; ISO 527 |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Modulus of Elasticity | 5.00 - 8.00 GPa | 725 - 1160 ksi | Injection and Compression; ISO 527 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Modulus of Elasticity | 5.00 - 8.00 GPa | 725 - 1160 ksi | Injection and Compression; ISO 527 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Modulus of Elasticity | 5.00 - 9.65 GPa | 725 - 1400 ksi | Average value: 7.89 GPa Grade Count:11 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-8099 PEEK, with mineral filler Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Reduced moment of inertia compared with metal parts.Chemical and hydrolysis resistance par.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-8279 PEEK, with CNT Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-8292 PEEK, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1301-7662/BK PPS, linear, with glass fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Improved fr.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1-8520 Polyamide 66, with carbon fiber, toughness-modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Elec.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 20/AF/15/TF/10 Polyphthalamide, with aramid reinforcement and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-8127-1 PEEK, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 527-2 |
Tisan TISOPLEN® 30% Glass Fiber Reinforced Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 178 |
Addiplast Addinyl B2 K20 Nylon 6 High density and high modulusInformation provided by Addiplast. |
|||
Modulus of Elasticity | 5.00 GPa @Temperature 100 °C |
725 ksi @Temperature 212 °F |
SIO 527 |
BASF Ultraform N 2200 G53 UNC Q600 25% Glass Filled POM Ultraform N2200 G53 UNC Q600 is a 25% glass fiber reinforced POM injection molding grade with enhanced stiffness and toughness. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | Conditioned; ISO 178 |
Addiplast Addinyl B2I V25 Flame Retardant Nylon 6, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, halogen freeInformation provided by Addiplast. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | Conditioned; ISO 178 |
Addiplast Addinyl PMD 20117 Flame Retardant Nylon, Glass Filled Flame retardant, glass fiver reinforced, friction resistantInformation provided by Addiplast. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | Conditioned; ISO 178 |
Addiplast Addinyl PMD 20164 Nylon 6 High resistance to repeated impactsInformation provided by Addiplast. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 527-2 |
Tisan TISOPLEN® 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 527-2 |
BASF Ultradur® B 4040 G2 10% Glass Filled PBT + PET Description: Is a PBT + PET, injection-molding grade containing 10% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, .. |
|||
Modulus of Elasticity | 5.00 - 13.3 GPa | 725 - 1930 ksi | Average value: 8.90 GPa Grade Count:22 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Modulus of Elasticity | 5.00 - 19.0 GPa | 725 - 2760 ksi | Average value: 10.2 GPa Grade Count:63 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-8339 PEEK, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 178 |
Addiplast Addinyl PMD 20170 Nylon 66 GalvanizingInformation provided by Addiplast. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 527-1/-2 |
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
Modulus of Elasticity | 5.00 GPa | 725 ksi | |
Lehmann & Voss PLASLUBE J-50/10/TF/15/BK Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated te.. |