- Lehmann & Voss LUVOCOM® 20/AF/15/TF/10 Polyphthalamide, with aramid reinforcement and PTFE
Lehmann & Voss LUVOCOM® 20/AF/15/TF/10 Polyphthalamide, with aramid reinforcement and PTFE
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Aramid Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 20/AF/15/TF/10 Polyphthalamide, with aramid reinforcement and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture and temperature to measures and electrical properties, compared with PA66Suitable for metall inserts.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 65.0 MPa | 9430 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.3 % | 2.3 % | flexural | |
| Modulus of Elasticity | 5.00 GPa | 725 ksi | |
| Flexural Strength | 94.0 MPa | 13600 psi | |
| Flexural Modulus | 4.50 GPa | 653 ksi | |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | edgewise; ISO 179 1eU |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| 195 °C | 383 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 330 °C | 608 - 626 °F | |
| Zone 1 | 320 - 340 °C | 608 - 644 °F | |
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |
| Zone 3 | 325 - 350 °C | 617 - 662 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 80.0 °C @Time 57600 sec |
176 °F @Time 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 18000 sec |
221 °F @Time 4.00 - 5.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (yellow) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 950A PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL ZM3242 PPE+PS (Asia Pacific)
- Goodfellow Niobium 99/Zirconium 1 Alloy
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- UBE UBEPOL VCR617 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Total Lumicene® mPE M 2310 EP Metallocene Polyethylene, Blown Film
- DSM Somos® 9110 Epoxy Photopolymer
- Solvay Specialty Polymers Algoflon® 15GR PTFE; Graphite Filled (discontinued **)
- DuPont Performance Polymers Hytrel® G4774 TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved