Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 4.00 - 6.00 GPa | 580 - 870 ksi | Compression; ISO 527 |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Modulus of Elasticity | 4.00 - 37.2 GPa | 580 - 5400 ksi | Average value: 15.3 GPa Grade Count:47 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7753/BL PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8135/VI PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8174 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 50/GF/10/TF/18/SI/2/GY5 Polycarbonate, with glass fiber, PTFE, lubricant modified Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 6-8548 Polyamide 12, with glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Suitable for discharging of statically generated electricity.Dynamic stressed parts.Low waterab.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | Sample Type 1B, 50 mm/min; ISO 527-1/2:1993 |
Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | DMA |
Lord Adhesives Thermosetâ„¢ ME-455-1 Epoxy Board Level Encapsulant LORD Thermosetâ„¢ ME-455-1 encapsulant is a low viscosity, one-component, semiconductor grade epoxy designed for the encapsulation of wire-bonded or flip chip die in PPGA, BGA, MCM and other cavi.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | Storage |
Lord Adhesives Thermosetâ„¢ ME-525 Underfill Encapsulant LORD Thermosetâ„¢ ME-525 encapsulant is a high purity, semiconductor grade epoxy underfill product developed for the encapsulation of flip chip devices. It is formulated to reduce warpage and wit.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105/BK0873 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Especially suitable for medical parts, super.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105/BK7308 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Suitable for biocompatible application.Not f.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105/BL8052 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105/GR/15/TF/15-2 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105/MS/15/TF/15 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-0856/GY7 PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-0950/RD PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7709/RD PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 19MB440 OPP Film Product Description: Bicor is a biaxially oriented transparent polypropylene film designed to be the outside web of a laminate.Availability: Africa & Middle East, Asia Pacific, Europe, Latin America.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 32MB600 OPP Film Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. Gives outstanding performance on overwrap and HFFS machines.Availability: Africa & Middle East, As.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 178 |
Addiplast Addilene H 211 V20 Polypropylene Homopolymer Glass fiber reinforced, high modulus and improved stiffnessInformation provided by Addiplast. |
|||
Modulus of Elasticity | 4.00 - 5.50 GPa | 580 - 798 ksi | |
Alliance BIF-17 Bonded (Composite) Magnetic Material |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
BASF Ultradur® S 4090 GM11 5/5% Glass/Mineral Filled PBT Description: Is a PBT + ASA, injection-molding grades reinforced with 5% glass fiber/mineral, for laminar parts with high demands on dimensional stability and low warpage, e.g. lids, ventilation gri.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
BASF Ultraform® N2720 M210 POM Description: Is a POM, product with increased stiffness and strength as well as good wear characteristics, used, for instance, for sliding chains and conveyor systems.Information provided by BASF |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | When curved |
Voloknohim PA-TM15 Glass and Mineral Filled Information provided by Voloknokhim |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8135/OR PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1-8228 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8344/GY PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |