Lehmann & Voss LUVOCOM® 1105/BK0873 PEEK, unreinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105/BK0873 PEEK, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceInherent flame resistance.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in | |
| Melt Flow | 42.24 g/10 min @Load 10.0 kg, Temperature 380 °C |
42.24 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 100 MPa | 14500 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 145 MPa | 21000 psi | |
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Coefficient of Friction, Static | 0.58 | 0.58 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 47.0 µm/m-°C | 26.1 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Oceanchem Group Brominated Epoxy Oligomers-1 (BEP-1)
- Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled
- Sylvin Technologies 9077-70 Natural PVC for Injection Molding
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- Dow STRANDFOAM™ EA 1600 Polypropylene Foam
- Arlon CP-322 Bulk Compound
- BASF Pluracol® 816 Molded Foam Polyol
- Denka VINYKON R3102 PVC, R grade for hard extrusion
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBTS
- Shamrock Technologies MicroFLON® 1437FG Thermoplastic Grade PTFE Additive
Copyright © lookpolymers.com All Rights Reserved