Addiplast Addilene H 211 V20 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass Reinforced, Impact Modified |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 211 V20 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, high modulus and improved stiffnessInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183/A |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | ISO 868 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO R 527 |
| Elongation at Yield | 2.5 % | 2.5 % | ISO R 527 |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | ISO 179/IeU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ISO 75-2/AF |
| Vicat Softening Point | 160 °C | 320 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | CEI 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2730 Amorphous Polyalphaolefin (APAO)
- PlastiComp Complet® LCF15/LGF35 – PA66 BLK Polyamide 66, 50% Long Carbon/Glass Fiber
- PolyOne Versalloy™ XL 9055-1 Thermoplastic Elastomer (TPE)
- Styrolution Novodur® HH-112 ABS
- Plastics Group Polifil® GFRMPPCC-40 40% Glass Reinforced Polypropylene, High Impact
- Universal Wire Works BAg-1 (AMS 4769) Silver Brazing Filler Metal
- Arlon 10842S085 Fully Cured, Unsupported Silicone Rubber
- 3M Nextel™ AF-10 Aerospace Woven Fabric 312
- Ashley Polymers Ashlene® 630-33G Nylon 6, 33% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved