- Polymer Property : Modulus of Elasticity = 435 ksi
Polymer Property : Modulus of Elasticity = 435 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO.178 DN.53452 |
| Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
| Modulus of Elasticity | 3.00 - 3.70 GPa @Temperature 60.0 - 150 °C |
435 - 537 ksi @Temperature 140 - 302 °F |
Average value: 3.44 GPa Grade Count:2 |
| Overview of materials for Polyetheretherketone, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Unreinforced". Each property range of values reported is minimum and maximum value.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1105-7198/BK PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1105-8173 PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1105-8319 PEEK, with PTFE, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts.Improved friction and wear behaviour. Emergency r.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1-1120 Polyamide 66, with PTFE, lubricant modified, high viscosity Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1301-8349 PPS, linear, with PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage, isotropic shrinkage .. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1-7177 Polyamide 66, with PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1-8379 Polyamide 66, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1850-7692 PBT, with glass spheres and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1850-7692/BK PBT, with glass spheres and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 19-7330 Polyamide 46, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Reduced moment of inertia compared with metal parts.Highly dimensionally stable at elevated tem.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 65-8452-1 PP-copolymer, with aramid reinforcement, lubricant modified Applications: Office communication.Low warpage, isotropic shrinkage characteristics.Dynamic stressed parts.Information provided by Lehmann & Voss & Co.KG |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 80-7695 Polyacetal-copolymer, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 |
| GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuou.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1100-7939/GY Polyether sulfone, unreinforced Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1800-7432 PET, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® G Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Isotropic shrinkage characteristics.Control disks, cams, sliding ele.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® GS-H/2 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Isotropic shrinkage characteristics.Control disks, cams, sliding ele.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1100-7721/WT9016 Polyether sulfone, unreinforced Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1105/TF/20/BN PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527-2 |
| BASF Ultraform® S1320 003 POM Description: Is a POM, free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thicknesses, higher stiffness and thermal stability.Informat.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| BASF Ultramid® B3UG4 Grey 22975 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 |
| BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Conditioned) Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 |
| BASF Ultramid® B3K PA6 (Dry) Ultramid B 3K is an easy flowing, stabilized for fast processing, grade of nylon 6. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | Conditioned; ISO 178 |
| Addiplast Addinyl C2 V15 Nylon 66/6, 15% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
| Modulus of Elasticity | 3.00 - 11.7 GPa | 435 - 1700 ksi | Average value: 6.79 GPa Grade Count:38 |
| Overview of materials for Acetal Copolymer + Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer + Glass/PTFE". Each property range of values reported is minimum and maximum values of .. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| BASF Ultramid® B3UG4 LS Grey 22985 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Lehmann & Voss LUVOCOM® 1-7497 Polyamide 66, with PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | Conditioned; ISO 178 |
| Addiplast Addinyl B2 ZV15 Nylon 6, 15% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||