GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Uncompounded |
| Manufacturer | GEHR Plastics Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuous operating temperature is from -15°C to 60°C. It can also be easily solvent, cemented and welded. Properties include: High mechanical strength, tensile strength and hardnessGood insulation properties for electronicsHigh chemical resistanceSelf-extinguishingLow water absorptionEasy to varnish and glueLow impact strengthLimited weather resistanceApplications include:Pumps and valve bodyGasketsBearing cagesPipe linesHand pump pipesBrush basic bodyParts in the dental medicineSeat stripsPipes for the mounting of kerfsLamp box PVC-ELS has improved electronical conductivity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | DIN 53505 |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Coefficient of Friction | 0.60 | 0.60 | DIN 53375 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 60.0 °C | 140 °F | |
| Minimum Service Temperature, Air | -15.0 °C | 5.00 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | VDE 0303 |
| Surface Resistivity per Square | <= 1.00e+16 ohm | <= 1.00e+16 ohm | VDE 0303 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | yes | |
| Aromatic Resistance | limited | |
| Bondability | yes | |
| CKW Resistance | no | |
| Color | Black | |
| Hydrocarbonate Resistance | yes | |
| Hydroxide Resistance | yes | |
| Ketone Resistance | no | |
| Physiological indifference according | no | |
| Resistance Against Hot Water | no | |
| UV Stabilization | no |
Users viewing this material also viewed the following:
- Johnson Matthey SW 850 Platinum w/ 15% Iridium Jewelry Alloy
- Zyvex Performance Materials Arovex™ 180 Carbon Nanotube Strengthened Prepreg
- ExxonMobil HDPE HD 9856B High Density Polyethylene Resin
- Buckeye Polymers BP PPC 0212 BLK Polypropylene Copolymer
- Carmel Olefins CAPILENE® HT 75 A Polypropylene Impact Copolymer
- Arlon R39091R036 0.036" (0.914 mm) Uncured Silicone Rubber with Nomex Fabric Substrate
- BASF Polystyrol® 168 N Polystyrene (Europe)
- ACC EP AEP EPI Engineered Polymers
- Chesterton 900 GoldEnd® Paste
- ExxonMobil SAE 30 Mobilgard 300
Copyright © lookpolymers.com All Rights Reserved