Lehmann & Voss LUVOCOM® 1105-8319 PEEK, with PTFE, easy flowing
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8319 PEEK, with PTFE, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts.Improved friction and wear behaviour. Emergency running property.Emergency running property, for highest tribologic needs.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in | |
| Melt Flow | 40.2 g/10 min @Load 2.16 kg, Temperature 380 °C |
40.2 g/10 min @Load 4.76 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 65.0 MPa | 9430 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 4.0 % | 4.0 % | flexural | |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Flexural Strength | 85.0 MPa | 12300 psi | |
| Flexural Modulus | 2.50 GPa | 363 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7950-9001-02 Thermoplastic Elastomer (TPE)
- LyondellBasell Petrothene® GA594189 Linear Low Density Polyethylene, Injection Molding Grade
- Michelman® Michem® Emulsion 34935 Anionic paraffin/ethylene acrylic acid wax emulsion
- Schwartz Technical Plastics LAMINEX® 2141 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled
- Solvay Specialty Polymers Galden® DET PFPE Fluid
- Vicone High Performance Rubber VicoSil™ 369DLK-GY High Performance Silicone Rubber
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N774 (SRF) Filler
- Denka VINYKON R3201 PVC, R grade for hard extrusion
- Fainplast Compounds CKL 76 Flexible PVC, Sheathing Lead Free
- 3M Scotchcal™ 8000-14 Graphic Film
Copyright © lookpolymers.com All Rights Reserved