- Lehmann & Voss LUVOCOM® 1100-7721/WT9016 Polyether sulfone, unreinforced
Lehmann & Voss LUVOCOM® 1100-7721/WT9016 Polyether sulfone, unreinforced
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-7721/WT9016 Polyether sulfone, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Superheated steam sterilizable.Inherent flame resistance.High quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 85.0 MPa | 12300 psi | |
| Elongation at Yield | 5.5 % | 5.5 % | |
| 7.3 % | 7.3 % | flexural | |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | |
| Coefficient of Friction, Static | 0.28 | 0.28 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 220 °C | 428 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | |
| Vicat Softening Point | 215 °C | 419 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | traffic white |
Users viewing this material also viewed the following:
- Ineos H13G-00 Polypropylene Homopolymer (discontinued **)
- Kraton® D1192 A (SBS) Liner Block Copolymer
- Solvay TECHNYL® B 230 PA66/6, DRY
- Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, Conditioned
- Teknor Apex APEX® 1008 Polyvinyl Chloride, Flexible
- Skamol Group SICAL 78 Silicon Nitride-Bonded Silicon Carbide Brick
- E-Polymers TEKAMID® TA210SG30 Impact Modified, 30% Glass Fiber Reinforced PA66, DAM
- Blue River Coatings High Performance Acrylic Topcoat
- Total Finathene® CD 481 HDPE conduit (discontinued **)
- Resinoid 7201 Phenolic Molding, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved