Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 172 MPa @Temperature 23.9 °C |
25000 psi @Temperature 75.0 °F |
Dry; ASTM D695 |
Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 285 Aramid Reinforced Nelcote® E-722 is a modified 350°F cure epoxy system with excellent processing characteristics for vacuum bag, press, and autoclave molding.Key Features and Benefits:Epoxy resin system optimized f.. |
|||
Compressive Strength | 172 MPa | 25000 psi | 10% Deformation; ASTM D695 |
Quadrant EPP Duratron® PI D7015G PI Bearing Grade Polyimide (ASTM Product Data Sheet) |
|||
Compressive Strength | 172 MPa | 25000 psi | Ultimate; TM R050-38 |
Resinlab® EP750 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP750 Clear is a two part unfilled epoxy structural adhesive which ingredients are listed in the Code of Federal Regulations Title 21 175.105 (Adhesives) and 175.300 (Resinous and polymer.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Break; TM R050-38 |
Resinlab® EP750 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP750 Clear is a two part unfilled epoxy structural adhesive which ingredients are listed in the Code of Federal Regulations Title 21 175.105 (Adhesives) and 175.300 (Resinous and polymer.. |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
Flatwise |
Industrial Laminates/Norplex ES-1 Engraving Stock Description: Composed of white melamine paper core with various pigmented cover sheets.Thickness Tested: 0.0620â€, 0.125â€, and 0.500†|
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
Flatwise |
Industrial Laminates/Norplex ES-2 Engraving Stock Description: Composed of black phenolic paper core, sub surfaces of white melamine, and various pigmented cover plies. |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
Flatwise |
Industrial Laminates/Norplex ES-3 Engraving Stock Description: Contains black phenolic/paper core and various colored covers impregnated with melamine resin. |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP101 Synthetic Fabric Description: Phenolic resin combined with spun nylon fabric. Good impact strength and excellent electrical properties under high humidity conditions. Meets applicable Boeing specification, but exemp.. |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP629 Paper Base Laminate Description: It is a paper-phenolic high-pressure laminate. It is intended primarily for mechanical applications and is suitable for electrical applications as well. Thickness Tested: 0.062", 0.125".. |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0... |
|||
Compressive Strength | 172 MPa @Thickness 12.7 mm |
25000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP318 Cotton Fabric Description: Post-forming canvas phenolic material. Mechanical and electrical properties similar to NP310E. It is made from a cotton fabric weighing more than 4 ounces per square yard and having a t.. |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Techmer ES Electrafil® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Techmer ES Electrafil® J-1/CF/30/TF/13/SI/2 Nylon 66, 30% Carbon Fiber, 13% PTFE, 2% Silicone |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Techmer ES Plaslube® J-1/20/MS/5 NAT PA66 |
|||
Compressive Strength | 172 MPa | 25000 psi | Maximum Static Bearing Load |
TriStar TriSteel AT Metal Backed PTFE Bearing System Ultraflon 601T (AT) POM bronze with PTFE, lined metal back bearing system, high PV, self lube, high speed. This liner will run with zero lubrication required. Most commonly used in clip bearings, li.. |
|||
Compressive Strength | 172 MPa | 25000 psi | 10% Deformation; ASTM D695 |
Ensinger Tecapeek® XP-119 Compression Molded PEEK Compound, 10% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Ensinger Tecatron® XP-64 Compression Molded PPS Compound, 40% Fiberglass Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p.. |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Ensinger Tecatron® XP-64B Compression Molded PPS Compound, 40% Fiberglass, Black Pigmented Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p.. |
|||
Compressive Strength | 172 MPa | 25000 psi | in plane |
Carlisle 201LL Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t.. |
|||
Compressive Strength | 172.4 - 241.4 MPa | 25000 - 35010 psi | ASTM C133 |
Ceradyne Thermo-Sil® UHS Fused Silica Fused Silica is an excellent thermal insulator with an extremely low coefficient of thermal expansion. It is excellent for thermal shock applications. The key characteristics of this material are:Hi.. |
|||
Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
Applied Composites 8041 Polyester SMC Industry Application: ElectricalProduct Application: Business MachinesDistinct Features: UL 94-VO, Radiant Panel |
|||
Compressive Strength | 172 MPa | 25000 psi | |
Aremco AREMCOLOX™ 502-1100 (Full-Fired) Dense Alumino-Silicate Good mechanical strength, and electrical and thermal resistance. For producing insulators, standoffs, feed-thrus, furnace carriers and brazing fixtures. Fabricate and fire yourself using conventio.. |
|||
Compressive Strength | 172 - 207 MPa | 25000 - 30000 psi | |
Bulk Molding Compounds BMC 8005 Polyester Molding Compound |
|||
Compressive Strength | 172 MPa | 25000 psi | Break; TM R050-38 |
Resinlab® EP1282 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Clear is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Ultimate; TM R050-38 |
Resinlab® EP1282 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Clear is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Break; TM R050-38 |
Resinlab® EP691 Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP691 is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has good wetting and ad.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Ultimate; TM R050-38 |
Resinlab® EP691 Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP691 is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has good wetting and ad.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Ultimate; TM R050-38 |
Resinlab® EP1115 Clear Unfilled Epoxy Adhesive Resinlab™ EP1115 Clear is a two part unfilled epoxy adhesive designed for bonding of metals, ceramics and most plastics. This product gives good resistance to water, salt spray, inorganic acids and.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Break; TM R050-38 |
Resinlab® EP1115 Clear Unfilled Epoxy Adhesive Resinlab™ EP1115 Clear is a two part unfilled epoxy adhesive designed for bonding of metals, ceramics and most plastics. This product gives good resistance to water, salt spray, inorganic acids and.. |
|||
Compressive Strength | 172 MPa | 25000 psi | Break; TM R050-38 |
Resinlab® EP1282 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Black is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |