Industrial Laminates/Norplex NP101 Synthetic Fabric

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP101 Synthetic Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Phenolic resin combined with spun nylon fabric. Good impact strength and excellent electrical properties under high humidity conditions. Meets applicable Boeing specification, but exempt from non-afterglow requirements.Thickness Tested: 0.062", 0125", and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.20 - 1.30 g/cc

@Thickness 1.57 mm
 1.20 - 1.30 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.30 %

@Thickness 1.57 mm
 0.30 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80 - 100

@Thickness 1.57 mm
 80 - 100

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 55.2 MPa

@Thickness 1.57 mm
 8000 psi

@Thickness 0.0620 in
 CW; ASTM D638
55.2 MPa

@Thickness 1.57 mm
 8000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 3.79 GPa

@Thickness 1.57 mm
 550 ksi

@Thickness 0.0620 in
 CW; ASTM D229
4.83 GPa

@Thickness 1.57 mm
 700 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 75.8 MPa

@Thickness 1.57 mm
 11000 psi

@Thickness 0.0620 in
 CW; ASTM D790
96.5 MPa

@Thickness 1.57 mm
 14000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 172 MPa

@Thickness 12.7 mm
 25000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 96.5 MPa

@Thickness 15.7 mm
 14000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 1.44 J/cm

@Thickness 12.7 mm
 2.70 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
1.82 J/cm

@Thickness 12.7 mm
 3.40 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 95.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 52.8 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 120 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 66.7 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 105 °C
221 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 3.75

@Thickness 1.57 mm
 3.75

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 19.7 kV/mm

@Thickness 1.57 mm
 500 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
25.6 kV/mm

@Thickness 1.57 mm
 650 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 45000 V

@Thickness 1.57 mm
 45000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
65000 V

@Thickness 1.57 mm
 65000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.035

@Thickness 1.57 mm
 0.035

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 17 sec

@Thickness 3.17 mm
 17 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 150 V

@Thickness 3.17 mm
 150 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1800 lb
0.5", ASTM D229
Color Natural