Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Premix Premi-Glas® 1200-25 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1200-25 is a fiberglass reinforced thermoset sheet molding compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Premix Premi-Glas® 1200H-25 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1200H-25 is a fiberglass reinforced thermoset sheet molding compound for general purpose and HVAC applications requiring thermal stability and stiffness.Key features and benefits are:Go.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ISO 527 |
Premix Thermoplastics PREBOARD E1025 Standard Epoxy Circuit Boards Standard epoxy (FR4) circuit boards do not lend themselves for high frequency applications due to the poor dielectric properties. For that reason PTFE is used predominately. This is an expensive mat.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Nylatron® 703XL PA 6 + internal lubricant, cast (ISO Data) This high performance cast nylon 6 bearing grade provides an even better wear resistance than Nylatron NSM, combined with good pressure-velocity capabilities and a near zero level of “stick-slip”... |
|||
Tensile Strength | 60.0 MPa | 8700 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Symalit® 1000 PVDF unfilled, extruded (ISO Data) Symalit 1000 PVDF is a highly crystalline unreinforced fluoropolymer combining good mechanical, thermal and electrical properties with excellent chemical resistance. It also shows good resistance to.. |
|||
Tensile Strength | 60.0 - 90.0 MPa | 8700 - 13100 psi | Compression; ISO 527 |
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Kolon KOCETAL® K200 Standard Grade Acetal Resin Suitable for both injection and extrusion.Applications: Injection and extruded use such as rod and sheetInformation provided by API Kolon. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Kolon SPESIN® KP212V0BLK Flame Retardant PBT Compound Resin Flame retardant, BLACKApplications: ConnectorsInformation provided by API-Kolon. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | Weld; ASTM D638 |
Kuraray Genestarâ„¢ GT2330 Nylon, 33% Glass Filled Toughness V-0 Grade. It is well suited for components requiring a high strength in pin fitting process, due to high ductility properties. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | GB/T 1040.2-2006 |
Sichuan Deyang Haton® hFR70 PPS / AR Polyphenylene Sulfide Injection molding, themal conductionInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Techmer ES Luriblend® TPX-PA6/6-95001 Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Techmer ES HiFill® ABS GF20 FR 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | dry; ISO 527 |
Ter Hell Plastic Terez® ABS 3320 A UV Acrylonitrile Butadiene Styrene Rapid flowing ABS with high impact strength, antistatic agent and UV stabilizer.Application: For all kinds of injection molding thin-walled parts.Information provided by Ter Hell Plastic GMBH. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D412 |
Lubrizol ESTANE® ETE50DT3 Ester Based Thermoplastic Polyurethane Features: Hard TPU with wide extrusion processing window and melt stability, low temperature flexibility, high transparency, UV stableUses: Extrusion: Hose and Tube, Profile, Cable Jacket; Injection.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | dry; ISO 527 |
Ter Hell Plastic Terez® PA 6.6 7750 T Polyamide 66 Description: Dry impact unfilled Polyamide 6.6, good flowability and demolding properties.Application: Molding parts of different kinds, high impact properties.Information provided by Ter Hell Plas.. |
|||
Tensile Strength | >= 60.0 MPa | >= 8700 psi | IEC 1212-2 5.7 |
Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm). Arc and tracking resistant.Information provided by Hippe. |
|||
Tensile Strength | >= 60.0 MPa | >= 8700 psi | IEC 1212-2 5.7 |
Hippe PF CP 205 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in electrical and electronic applications. Good stability of electrical properties under high humidity. Also available in cold or hot-punching versions. Flame retardant.Information provided .. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | DIN 53 455 |
Hippe PMMA Components made of PMMA are brilliantly transparent. Outstanding aging stability and weathering resistance. Good surface hardness. Abrasion-resistant. Physiologically safe. High strength. Easi.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | cond.; DIN 53 455 |
Hippe PA 6 G Thick-wall pre-forms, heavy semi-finished products. Transfusion of inserts (rolls, cores) and all types of large preforms.Information provided by Hippe. |
|||
Tensile Strength | >= 60.0 MPa | >= 8700 psi | IEC 1212-2 5.7 |
Hippe PF CC 202 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm).Information provided by Hippe. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | 50 mm/min; ISO 37 |
BASF Elastollan R 2001 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |
|||
Tensile Strength | 60.0 MPa @Strain 8.00 %, Temperature 40.0 °C |
8700 psi @Strain 8.00 %, Temperature 104 °F |
50 mm/min; ISO 527-2 |
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |
|||
Tensile Strength | 60.0 - 79.3 MPa | 8700 - 11500 psi | ASTM D638 |
Cast Nylons Nycast® CP Caprolactam/Laurinlactum Copolymer Cast Nylon Highly resilient, with higher tensile elongation and impact strength than standard grades, NYCAST® CP is used applications requiring an extra degree of toughness. A copolymer of caprolactam and lau.. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Aaron Industries AAROPRENE® AEPC 5000-1 Engineered Polycarbonate Resin Melt flow index may be specified. |
|||
Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
Aaron Industries AAROPRENE® AEPC 5000-4 Engineered Polycarbonate Resin Melt flow index may be specified. |