- Sichuan Deyang Haton® hFR70 PPS / AR Polyphenylene Sulfide
Sichuan Deyang Haton® hFR70 PPS / AR Polyphenylene Sulfide
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hFR70 PPS / AR Polyphenylene Sulfide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, themal conductionInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 60.0 MPa | 8700 psi | GB/T 1040.2-2006 |
| Elongation at Break | 0.30 % | 0.30 % | GB/T1040.2-2006 |
| Flexural Strength | 140 MPa | 20300 psi | GB/T 9341-2008 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.20 W/m-K | 8.33 BTU-in/hr-ft²-°F | ISO 22007-4 |
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 2.00e+15 ohm | 2.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7680-1 (Natural) Thermoplastic Elastomer (TPE)
- Lehmann & Voss LUVOCOM® 19-8250 Polyamide 46, lubricant modified
- IRPC Polimaxx Polene 129PC Styrene Acrylonitrile
- SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific)
- Special Metals NILO® Alloy 48 Controlled-Expansion Alloy
- Borealis HD244CF Polypropylene
- Westlake Hifor LT74105 Linear Low Density Polyethylene
- Zoltek Panex 30® High Twist Carbon Roving
- Ascend Performance Materials Vydyne® 20NSP Nylon 66, Conditioned
- BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved