- Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet
Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet
| Category | Polymer , Thermoset , Melamine |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm). Arc and tracking resistant.Information provided by Hippe.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 - 1.50 g/cc | 1.30 - 1.50 g/cc | IEC 1212-2 8.1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 60.0 MPa | >= 8700 psi | IEC 1212-2 5.7 |
| Flexural Strength | >= 70.0 MPa | >= 10200 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
| Flexural Modulus | >= 5.00 GPa | >= 725 ksi | IEC 1212-2 5.2 |
| Compressive Strength | >= 90.0 MPa | >= 13100 psi | Perpendicular to laminations; IEC 1212-2 5.3 |
| Shear Strength | >= 45.0 MPa | >= 6530 psi | Parallel to laminations; IEC 1212-2 5.6 |
| Izod Impact, Unnotched (ISO) | >= 2.50 kJ/m² | >= 1.19 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.3 |
| Charpy Impact Unnotched | >= 0.300 J/cm² | >= 1.43 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 | V-0 | IEC 1212-2 7.2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+7 ohm | >= 1.00e+7 ohm | After immersion in water; IEC 1212-2 6.3 |
| Dielectric Constant | <= 8.0 @Frequency 48.0 - 62.0 Hz |
<= 8.0 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 8.0 @Frequency 1.00e+6 Hz |
<= 8.0 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Dielectric Breakdown | >= 15000 V @Temperature 90.0 °C |
>= 15000 V @Temperature 194 °F |
In oil, parallel to laminations; IEC 1212-2 6.2 |
| Dissipation Factor | <= 0.030 @Frequency 48.0 - 62.0 Hz |
<= 0.030 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 0.030 @Frequency 1.00e+6 Hz |
<= 0.030 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Comparative Tracking Index | >= 500 V | >= 500 V | IEC 1212-2 6.4 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Proof Tracking Index | 500 | IEC 1212-2 6.4 |
| Thermal Endurance | 130 T.I. | IEC 1212-2 7.1 |
| Water Absorption | < 305 mg | IEC 1212-2 8.2; Test piece 50 x 50 x 10 mm |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4935 TPE, Transparent
- LG Chemical SSBR 2550 High Acrylonitrile Polymer
- Techmer ES HiFill® PP 0320 S1 Polypropylene
- Unitika elitel UE3250 Polyester, Pellet
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Mistron Vapor Filler
- 3M 3187 (Clear) Polyethylene Protective Tapes
- BASF Ultrason E 6020 P PES
- Albis Plastics Tedur® L 9510-1 PPS, 40% Glass Fiber
- Ascend Performance Materials Vydyne® 66Z Nylon 66, DAM
- BASF N-Methyldiethanolamine
Copyright © lookpolymers.com All Rights Reserved