Hippe PA 6 G
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe PA 6 G.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thick-wall pre-forms, heavy semi-finished products. Transfusion of inserts (rolls, cores) and all types of large preforms.Information provided by Hippe.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | DIN 53 479 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | Absorption of humidity in standard operating environment; DIN 53 715 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | DIN 53 495 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa @Time 30.0 sec |
24700 psi @Time 0.00833 hour |
DIN 53 456 |
| Tensile Strength | 60.0 MPa | 8700 psi | cond.; DIN 53 455 |
| 85.0 MPa | 12300 psi | dry; DIN 53 455 | |
| Elongation at Break | 5.0 % | 5.0 % | dry; DIN 53 455 |
| 50 % | 50 % | cond.; DIN 53 455 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | cond.; DIN 53 457 |
| 4.00 GPa | 580 ksi | dry; DIN 53 457 | |
| Coefficient of Friction, Dynamic | 0.36 - 0.43 | 0.36 - 0.43 | Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | |
| Melting Point | 220 °C | 428 °F | DIN 53 736 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous use |
| 180 °C | 356 °F | Short Periods | |
| Glass Transition Temp, Tg | 5.00 °C | 41.0 °F | cond., dynamic; DIN 53 736 |
| 40.0 °C | 104 °F | dry, dynamic; DIN 53 736 | |
| Flammability, UL94 | HB | HB |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | blue, nat., black | |
| Creep Resistance | Grade CTI 600 | DIN 53 480, IEC-112, VDE 0303 Part 1 |
| Resistance to hot water, suds | resistant in some conditions |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Rynite® FR515 BK507 PET (Unverified Data**)
- Mallard Creek Polymers Rovene® 6126 Styrene-Acrylic Emulsion
- Isoflon Tisoflon® 10S Silicone Coated Glass Fabric
- SABIC Innovative Plastics LNP LUBRILOY DF202P PC
- Hexcel® HexTow™ AS4C Carbon Fiber
- American Elements Copper Oxide Nanopowder
- DuPont™ Kapton® 100A Polyimide Film, 25 Micron Thickness
- Eurostar Staramide PFB33 PA6, 20% Glass Fiber, 10% Glass Bead Filled, Injection Molding Resin
- AorTech Biomaterials ECSil™ 90A Biomedical Carbonate Silicone Pellets
- DuPont Performance Polymers Hypalon® CP-826 Adhesion Primer, General Description (discontinued **)
Copyright © lookpolymers.com All Rights Reserved