Techmer ES Luriblend® TPX-PA6/6-95001
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® TPX-PA6/6-95001.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm @Thickness 3.17 mm |
0.019 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ASTM D785 |
| Tensile Strength | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Yield | 16 % | 16 % | ASTM D638 |
| Flexural Yield Strength | 97.2 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm |
1.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 10.1 J/cm @Thickness 3.17 mm |
19.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 97.2 µm/m-°C | 54.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Pyrotek J-1 Ropes
- Overview of materials for Polyphthalamide (PPA), Carbon Fiber
- Polyram RamTough RZ720 Polycarbonate, UV Stabilized
- Cossa Polimeri ESTACARB 1560 V0 HF Flame Retardant Polycarbonate
- ExxonMobil Mobil Zerice 46 S Oil
- Colorite Polymers 9904 Clear Extrusion Vinyl Compound
- E-Polymers TEKALOY® G70NHT Non Halogen Flame Retardant Impact Resistance PC/ABS Alloy
- BASF N-(2-Aminoethyl) ethanolamine
- Astro Met AmAlOx 87 Alumina - Aluminum Oxide
- A. Schulman POLYBLAK™ 4692 Premium Black Color Concentrate, 35% Carbon Black Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved