Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 85.0 MPa | 12300 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Ertalon® 66 GF30 PA 66, 30% glass filled, extruded (ISO Data) Compared with virgin PA 66, this 30 % glass fibre reinforced and heat stabilised nylon grade offers increased strength, stiffness, creep resistance and dimensional stability whilst retaining an exce.. |
|||
Tensile Strength | 85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66
(Unverified Data**) Minlon® 11C40 BKB086 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ASTM D638 |
Kolon KOPA® KN333HRBL Heat Resistant Nylon 66 Middle viscosity, BLACKApplications A variety of reservoir tanks and housingsInformation provided by API-Kolon. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ISO 527 |
Lucite International Diakon® CMH454 Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ISO 527 |
Lucite International Diakon® CMH454L Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ISO 527 |
Lucite International Diakon® MH254 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® QC200N Polyphenylene Sulfide (PPS) Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and.. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® QC200P Polyphenylene Sulfide (PPS) Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and.. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® QC220N Polyphenylene Sulfide (PPS) Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and.. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® QC220P Polyphenylene Sulfide (PPS) Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and.. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | 50 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 226 Nylon 6.6 SAXAMID 226 is a general purpose polyamide 6.6 injection-molding-grade. Benefits are short cycle times and good release properties.Information provided by SAX Polymers |
|||
Tensile Strength | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527-1 |
Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled SAXALEN PPH305G30 is a 30% glass filled Polypropylene - Homopolymer injection molding grade with high stiffness, low creep under load and good flow properties.Information provided by SAX Polymers |
|||
Tensile Strength | 85.0 MPa @Thickness >=1.50 mm |
12300 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear.. |
|||
Tensile Strength | 84.8 MPa | 12300 psi | ASTM D638 |
Ensinger Tecapeek® XP-115 Compression Molded PEEK Compound, Static Dissipative Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Tensile Strength | 84.8 MPa | 12300 psi | ASTM D638 |
Ensinger Tecapeek® XP-181 Compression Molded PPEK Compound, EWS Filled and Carbon Fiber Reinforced Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Tensile Strength | 84.8 MPa | 12300 psi | ASTM D638 |
Ensinger Tecapeek® XP-91BHT Compression Molded PEEK HT Compound, 30% Fiberglass, Black Pigmented Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Tensile Strength | 84.8 MPa | 12300 psi | ASTM D638 |
Ensinger Tecapeek® XP-99 Compression Molded PEEK Compound, Bearing Grade Material with 7% Graphite, 8% PTFE, and 15% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Tensile Strength | >= 85.0 MPa | >= 12300 psi | IEC 1212-2 5.7 |
Hippe PF CC 203 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet Used in mechanical applications (fine weave: =130 g/m2, >30 threads/cm). Recommended for small parts. Better mechanical properties and poorer electrical properties than type PF CC 204.Information .. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | dry; DIN 53 455 |
Hippe PA 6 G Thick-wall pre-forms, heavy semi-finished products. Transfusion of inserts (rolls, cores) and all types of large preforms.Information provided by Hippe. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | DIN 53 455 |
Hippe PEI A material with very high mechanical strength and high thermoforming stability which can be used at high temperatures. Distinguished by constant dielectric properties, a wide range of frequency and .. |
|||
Tensile Strength | 85.0 MPa | 12300 psi | cond.; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Tensile Strength | 85.0 MPa @Strain 15.0 %, Temperature 0.000 °C |
12300 psi @Strain 15.0 %, Temperature 32.0 °F |
50 mm/min; ISO 527-2 |
BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |