BASF Elastollan R 2000 20% Glass Filled TPUR

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer BASF
Trade Name Elastollan
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Elastollan R 2000 20% Glass Filled TPUR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expansion comparable with steel and aluminum, low mold shrinkage and ease of painting. Typical Applications: Automotive body and rocker panels, underbody sealants, technical moldings e.g. plugs and ski tips.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183-1-A
Mechanical Properties Metric English Comments
Hardness, Shore D 67
67
ISO 686
Tensile Strength 65.0 MPa
9430 psi
50 mm/min; ISO 37
35.0 MPa

@Strain 5.00 %,
Temperature 60.0 °C
 5080 psi

@Strain 5.00 %,
Temperature 140 °F
 50 mm/min; ISO 527-2
40.0 MPa

@Strain 5.00 %,
Temperature 40.0 °C
 5800 psi

@Strain 5.00 %,
Temperature 104 °F
 50 mm/min; ISO 527-2
42.0 MPa

@Strain 10.0 %,
Temperature 60.0 °C
 6090 psi

@Strain 10.0 %,
Temperature 140 °F
 50 mm/min; ISO 527-2
42.0 MPa

@Strain 20.0 %,
Temperature 60.0 °C
 6090 psi

@Strain 20.0 %,
Temperature 140 °F
 50 mm/min; ISO 527-2
50.0 MPa

@Strain 10.0 %,
Temperature 40.0 °C
 7250 psi

@Strain 10.0 %,
Temperature 104 °F
 50 mm/min; ISO 527-2
54.0 MPa

@Strain 20.0 %,
Temperature 40.0 °C
 7830 psi

@Strain 20.0 %,
Temperature 104 °F
 50 mm/min; ISO 527-2
55.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 7980 psi

@Strain 5.00 %,
Temperature 73.4 °F
 50 mm/min; ISO 527-2
69.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 10000 psi

@Strain 10.0 %,
Temperature 73.4 °F
 50 mm/min; ISO 527-2
69.0 MPa

@Strain 20.0 %,
Temperature 23.0 °C
 10000 psi

@Strain 20.0 %,
Temperature 73.4 °F
 50 mm/min; ISO 527-2
80.0 MPa

@Strain 5.00 %,
Temperature 0.000 °C
 11600 psi

@Strain 5.00 %,
Temperature 32.0 °F
 50 mm/min; ISO 527-2
85.0 MPa

@Strain 15.0 %,
Temperature 0.000 °C
 12300 psi

@Strain 15.0 %,
Temperature 32.0 °F
 50 mm/min; ISO 527-2
88.0 MPa

@Strain 10.0 %,
Temperature 0.000 °C
 12800 psi

@Strain 10.0 %,
Temperature 32.0 °F
 50 mm/min; ISO 527-2
Elongation at Break 25 %
25 %
50 mm/min; ISO 37
Charpy Impact Unnotched 11.0 J/cm²

@Temperature -30.0 °C
 52.3 ft-lb/in²

@Temperature -22.0 °F
 DIN ISO 179
14.0 J/cm²

@Temperature 23.0 °C
 66.6 ft-lb/in²

@Temperature 73.4 °F
 DIN ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 DIN ISO 179
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 DIN ISO 179
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 176 °F
 53752-A
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
DIN EN ISO 75-2/Be
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
DIN EN ISO 75-2/Ae
Vicat Softening Point 92.0 °C
198 °F
B/50; ISO 306
Processing Properties Metric English Comments
Processing Temperature 225 - 245 °C
437 - 473 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Descriptive Properties Value Comments
Color Natural
Commercial Status North America
Primary Processing Technique Injection molding