Polymer Property : Linear Mold Shrinkage, Flow = 0.0030 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing 30% Mixed Glass, 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON DE0021E PC (Asia Pacific) LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON DE0029EF PC LNP STAT-KON* DE0029EF is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Flame Retardant, Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON DE002ER PC LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON EE004 PEI LNP* STAT-KON* EE004 is a compound based on Polyetherimide resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Asia Pacific) LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific) LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.20 mm	0.0010 - 0.0030 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® PDR4911 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.20 mm	0.0010 - 0.0030 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® VIC4350 PBT (Asia Pacific)
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON REP349 PA 66 LNP* STAT-KON* REP349 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone, 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp DF0069E PC LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp DF0069E PC (Asia Pacific) LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp EC002E PEI LNP THERMOCOMP* EC002E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp EC002E PEI (Asia Pacific) LNP THERMOCOMP* EC002E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP EC004XXC PEI LNP* THERMOCOMP* EC004XXC is a compound based on Polyetherimide resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP EC004XXC PEI (Asia Pacific) LNP* Thermocomp* EC004XXC is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific) LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific) LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm @Time 86400 sec	0.0020 - 0.0030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK (Asia Pacific) LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Linear Mold Shrinkage, Flow	0.0021 - 0.0030 cm/cm @Time 86400 sec	0.0021 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP SF006 PA 12 LNP THERMOCOMP* SF006 is a compound based on Nylon 12 resin containing 30% Glass Fiber.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11 LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6 LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture.
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm @Time 86400 sec	0.0020 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp SF006S PA 12 LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re..
Linear Mold Shrinkage, Flow	0.0021 - 0.0030 cm/cm @Time 86400 sec	0.0021 - 0.0030 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermocomp SF006S PA 12 LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Verton WV00A PBT (Europe-Africa-Middle East) LNP VERTON* WV00A is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.