SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 122 MPa | 17700 psi | ASTM D638 |
| 123 MPa | 17800 psi | ISO 527 | |
| Elongation at Break | 3.9 % | 3.9 % | ISO 527 |
| 4.9 % | 4.9 % | ASTM D638 | |
| Tensile Modulus | 7.60 GPa | 1100 ksi | 1 mm/min; ISO 527 |
| 9.28 GPa | 1350 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 192 MPa | 27800 psi | ISO 178 |
| 220 MPa | 31900 psi | ASTM D790 | |
| Flexural Modulus | 7.97 GPa | 1160 ksi | ISO 178 |
| 8.48 GPa | 1230 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.28 J/cm | 23.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 88.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP FR 7C11 Polypropylene, Unspecified (PP, Unspecified)
- Omya OMYACARB® 100 - PT Calcium Carbonate
- SABIC Innovative Plastics ULTEM ATX200R PEI Blend (Europe-Africa-Middle East)
- UBE UBEPOL BR34HL HIPS (stirring rate = 400 rpm)
- Polyplastics Duranex® C5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled
- Toyobo Diaflora® BD 2080B
- Covestro Makrolon® 2408 Polycarbonate
- Barlog Plastics KEBAFORM C 90.0 POM Copolymer unreinforced
- SABIC Innovative Plastics Lexan® 243R PC
- Solvay Specialty Polymers Veradel® AG-320 Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved