SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| 1.354 g/cc | 0.04892 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.310 % | 0.310 % | 50% RH, 24 hrs; ASTM D570 |
| 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
| 165 MPa | 23900 psi | ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 3.4 % | 3.4 % | ISO 527 | |
| Tensile Modulus | 11.6 GPa | 1680 ksi | 1 mm/min; ISO 527 |
| 12.2 GPa | 1770 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 244 MPa | 35400 psi | ASTM D790 |
| 262 MPa | 38000 psi | ISO 178 | |
| Flexural Modulus | 9.58 GPa | 1390 ksi | ASTM D790 |
| 12.0 GPa | 1740 ksi | ISO 178 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.05 J/cm | 20.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 72.0 kJ/m² | 34.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 19-7277 Polyamide 46, with carbon fiber and PTFE
- Multibase Multi-Flex® D 5308 TPO Thermoplastic Polyolefin Elastomer
- Lehmann & Voss LUVOCOM® 100-7846 Thermoplastic polyurethane, with aramid reinforcement
- Wellman Wellamid® FRGFT1741-BK2 Nylon 66, 32% Glass Fiber Reinforced, Flame Retardant
- Wieland 1410 Wilaform Gold
- Dow Corning LSPYW31 SILICONE MASTERBATCH YELLOW
- DSM Akulon® K224-HG3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Dry)
- ATI Allegheny Ludlum 309S Austenitic Stainless Steel
- 3M 5481 PTFE Skived Film Tape
Copyright © lookpolymers.com All Rights Reserved