SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| 1.388 g/cc | 0.05014 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | ISO 527 |
| 196 MPa | 28400 psi | ASTM D638 | |
| Elongation at Break | 1.1 % | 1.1 % | ISO 527 |
| 1.3 % | 1.3 % | ASTM D638 | |
| Tensile Modulus | 19.44 GPa | 2820 ksi | 50 mm/min; ASTM D638 |
| 20.87 GPa | 3027 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 269 MPa | 39000 psi | ISO 178 |
| 280 MPa | 40600 psi | ASTM D790 | |
| Flexural Modulus | 17.93 GPa | 2601 ksi | ISO 178 |
| 18.17 GPa | 2635 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.73 J/cm | 6.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 151 x 10-8 mm³/N-M | 75.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural
- Ensinger ENSITEP® PBT Polybutylene Terephthalate - Extruded Products (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7713-NA Polyacetal-copolymer, with carbon fiber and PTFE
- Garlock 9405 PTFE Rubber Sheet, 25% Glass Filled
- Industrial Laminates/Norplex NP101 Synthetic Fabric
- Teknor Apex APEX® 3301-70 Polyvinyl Chloride, Flexible
- ConocoPhillips Conoco® El Mar® Ashless Heavy Duty Oil, SAE Viscosity Grade 40
- Ashley Polymers Ashlene® 62M Nylon 66, 40% Mineral reinforced
- Applied Nanostructured Solutions Carbon NanoStructure Chopped Fiber
- BASF 2-Mercaptoethanol
Copyright © lookpolymers.com All Rights Reserved