Styron INSPIREâ„¢ TF1301 Thermoplastic Polyolefin
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | Styron |
| Trade Name | INSPIRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron INSPIREâ„¢ TF1301 Thermoplastic Polyolefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.965 g/cc | 0.0349 lb/in³ | ASTM D792B; ISO 1183 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 16.2 MPa | 2350 psi | ASTM D638; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | ASTM D638; ISO 527-2 |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D709A |
| Izod Impact, Notched | NB | NB | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | unannealed; ASTM D648; ISO 75-2/B |
Users viewing this material also viewed the following:
- Garlock 362 Nitrile Sheet Rubber
- Materion Beryllium Copper Alloy M25 Rod and Bar; HT (TH04) Temper; over 25.4 to 76 mm (UNS C17300)
- Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F)
- Schott FG3 Conversion Filter
- Shakespeare WN-38 diameter 0.4 mm Nylon 6 Monofilament
- Schmolz + Bickenbach UGIMA® 304 Cu Stainless Steel Bar
- Lubrizol Estane® T460AH Thermoplastic Polyurethane
- Enviro Tech International EnSolv® Ionic n-Propyl Bromide Vapor Degreasing Solvent
- TSE Industries Millathane® CM High Temperature-Resistant Millable Polyester Polyurethane
Copyright © lookpolymers.com All Rights Reserved