LyondellBasell Hifaxâ„¢ CA387 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CA387 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifax â„¢ CA387 is a thermoplastic polyolefin elastomer suitable for automotive exterior partsFeatures: Good StiffnessGood ProcessabilityGood Impact ResistanceGood Colorability PaintableHigh FlowDurableInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | ISO 1183 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1, -2 |
| Flexural Modulus | 0.951 GPa | 138 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.60 kJ/m² @Temperature -40.0 °C |
3.62 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 42.0 kJ/m² @Temperature 10.0 °C |
20.0 ft-lb/in² @Temperature 50.0 °F |
ISO 180 | |
| 46.0 kJ/m² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
Instrumented; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature -30.0 - 100 °C |
55.6 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.1 % | 1.1 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.50 % @Temperature 121 °C, Time 3600 sec |
1.50 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Lucas-Milhaupt BRAZE 630 Silver Based Cadmium Free Filler Metal
- Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite
- Sumitomo Chemical ESPOLEX® 4832 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Canyon 10277U/4 Concentrate Based In LLDPE
- PlastxWorld CEVIAN® LMW48 Laser Markable Grade ABS
- DuPont Performance Polymers Rynite® FC01 BK507 Polyethylene Terephthalate (PET) (Unverified Data**)
- Colorite Polymers 7077 Non-Phthalate 77 Series Vinyl Compound
- Dow Corning 340 Heat Sink Compound
- 3M 25A26 Co-Extruded Polyethylene Protective Tapes
- BASF Neopor® 2300 Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved