Polymer Property : Melt Flow = 12 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
SABIC Innovative Plastics Lexan® OQ4320 PC (Europe-Africa-Middle East) LEXAN OQ4320 is a medium viscosity grade with a UV cut-off up to 400 nm and a greater optical purity than standard grades. Fields of application for this material are optical lenses, f.i. in sunglas..
Melt Flow	12 g/10 min @Load 5.00 kg, Temperature 200 °C	12 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
LG Chemical SF-510 Alphalac Polystyrene (Unverified Data**) Super flow, High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include TV cabinets, thin pa..
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
SABIC Innovative Plastics Lexan® FXM921A PC (Europe-Africa-Middle East) LEXAN FXM921A is a transparent/translucent, medium viscosity, flame retardant grade with a metallic-luster appearance. Color package may affect performance.This data was supplied by SABIC-IP for the..
Melt Flow	12 g/10 min	12 g/10 min	Condition 190/2.16; ASTM D1238
Chevron Phillips HiD® 94312 HDPE Extrusion Coating Resin (discontinued **) Resin Type: Melt blend, FDA approvedCharacteristics: Good processabilityGood drawdown capabilityImproved MVTR propertiesGrease resistanceApplications: MVTR applicationsRelease linersCup stockInforma..
Melt Flow	12 g/10 min @Temperature 190 Â°C	12 g/10 min @Temperature 374 Â°F	ASTM D1238
Kolon KOPELÂ® KP3340 General Purpose TPE Resin KOPELÂ® is a thermoplastic polyester elastomer which is a new engineering rubber having combined properties of conventional rubber and thermoplastic. Its flexibility and elastic recovery are very..
Melt Flow	12 g/10 min @Load 5.00 kg, Temperature 200 Â°C	12 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
LG Chemical 401 AF Flame Retardant HIPS NON-DECA, Flame retardant, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, uses non-bromide as fl..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 Â°C	12 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Ineos L12N-00 Polypropylene Impact Copolymer This is a medium melt flow rate, nucleated impact copolymer polypropylene for injection molding and compounding applications. This material meets the requirements of the U.S. Food and Drug Administ..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 Â°C	12 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding Key Characteristics:High clarityHigh stiffnessGood processabilityMicrowavable for cooking applicationsOdorlessSafe for food contactRecommended Applications:General purpose injection parts that requi..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Teknor Apex TEKRON® 4300-D88F Thermoplastic Elastomer Information provided by Teknor Apex Company
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis CG9620 High Density Polyethylene CG9620 is a high density polyethylene film grade which combine excellent extrusion behavior with superior mechanical properties. Applications: CG9620 is recommended for coated film and co-extrusion..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 4535 is a blue color concentrate based in polyethylene . This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 4535 is typi..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ Blue Tint P40530 Concentrate Based In Homopolymer Polypropylene DescriptionPOLYBATCH® P40530 is a blue tint color concentrate based in homopolymer polypropylene. This concentrate was designed to provide color in blow molding applications. POLYBATCH® P40530 i..
Melt Flow	12 g/10 min	12 g/10 min	ASTM D1238L
Total PPH 3620WZ Polypropylene, Injection Molding Grade Injection molding homopolymerNucleation - FINA 3620WZ is engineered with nucleation to provide fast cycle time and improve contact clarity in thin wall multi- cavity molds.Antistat - FINA 3620WZ con..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ Grey 8368 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 8368 is a grey color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 8..
Melt Flow	12 - 20 g/10 min	12 - 20 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman.
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Unipetrol PP MONSTEN® MT 812 Polypropylene Random Copolymer Made for injection molding applications. Antistatic and transparent stabilization. Random copolymer.Information provided by Unipetrol RPA
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ Grey 8368 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 8368 is a grey color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 8..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D 1238
Cossa Polimeri ESTAPROP 1000 V2 H Flame Retardant Polypropylene PP homopolymerFlame retardant class V2, PBDE free, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
ExxonMobil Exxtral™ HMU 208 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness and release agent for automotive HVAC and under-the-hood applications.Availability: Africa & Middl..
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Diamond Polymers PC-1212FRO Natural, Flame Retardant Polycarbonate Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	12 g/10 min @Load 1.00 kg, Temperature 235 °C	12 g/10 min @Load 2.20 lb, Temperature 455 °F
Arkema Group Pebax® 3533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 35 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness..
Melt Flow	12 g/10 min	12 g/10 min	ASTM D1238
Aclo Accutech Polypropylene Homopolymer HP0336T20L Talc Reinforced
Melt Flow	12 g/10 min	12 g/10 min	ASTM D1238
Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Braskem TI6120Q4 High Impact Copolymer Polypropylene Description: Extra High Izod Impact, Superior Low Temperature Drop Impact, Good Paint AdhesionApplications: Suggested Uses Include Compounding, Automotive, Injection MoldingThis resin meets the requ..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 °C	12 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Carmel Olefins CAPILENE® R 50 Polypropylene Homopolymer CAPILENE® R 50 is a polypropylene homopolymer intended for injection molding, characterized by good flow properties combined with good balance of stiffness and impact. APPLICATIONS CAPILENE ® ..
Melt Flow	12 g/10 min	12 g/10 min	ASTM D359
Asahi Glass Fluon® C-88AXP ETFE Fluororesin A thermoplastic fluoropolymer developed by Asahi Glass. It is a copolymer comprising of tetrafluoroethylene and ethylene. Fluon® ETFE is a balanced fluoropolymer that has chemical resistance and el..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 8760 is a grey color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 8..
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Lucent Polymers POM-500 Acetal Homopolymer, General Purpose, Injection Grade Add "U" for UV StabilizedInformation provided by Lucent Polymers, Inc.
Melt Flow	12 g/10 min	12 g/10 min
Zeon Chemicals Quintac® 3433N SIS Block Polymer Styrene Isoprene (SIS) Block Polymer. Information provided by Zeon Chemicals L.P.
Melt Flow	12 g/10 min @Load 5.00 kg, Temperature 200 °C	12 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
Ineos Nova 204L Crystal Polystyrene General Purpose Grade (discontinued **) Fast cycling, Good heat resistance, Good balance of properties and flow characteristics, Extrusion and Injection Molding Applications: General purpose injection molded itemsProperties were determin..