SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High clarityHigh stiffnessGood processabilityMicrowavable for cooking applicationsOdorlessSafe for food contactRecommended Applications:General purpose injection parts that require high clarity and good dimensional stability such as food containers, toys and closureInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 2.00 mm |
0.015 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Modulus | 1.67 GPa | 242 ksi | ASTM D790 |
| Izod Impact, Notched | 0.196 J/cm @Temperature 0.000 °C |
0.367 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 0.343 J/cm @Temperature 23.0 °C |
0.643 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 20 % @Thickness 1.00 mm |
20 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 65 % @Thickness 1.00 mm |
65 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREBOARD E1025 Standard Epoxy Circuit Boards
- Polymer Resources PC-FD4-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold Release, Gamma Resistant
- Gichem GILAC H120X6/VOU ABS Flame Retardant (discontinued **)
- LG Chemical LUCEL VC127-LD Antistatic POM, Unreinforced, High Flow, For VCR Reels
- Lehmann & Voss LUVOCOM® 1105/MS/15/TF/15 PEEK, with PTFE, lubricant modified
- Chase Plastics CP Pryme® N320GL (DAM) Nylon 6 (Utility Grade), 20% Glass Fiber Reinforced, Internally Lubricated
- CoorsTek PlasmaPure-UC™ 99.9% Alumina
- Eurofoam Polycell PLZ 45 Polyethylene Foam
- Solvay RHODASURF® ID/79 Surfactant
Copyright © lookpolymers.com All Rights Reserved