Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 54 | 54 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.900 GPa | 275.5 ksi | ASTM D638 |
| Flexural Strength | 29.0 MPa | 4210 psi | ASTM D790 |
| Flexural Modulus | 1.950 GPa | 282.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T25020 Polypropylene Copolymer, Mineral Reinforced
- Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified
- Multibase Multi-Flex® D 2010 TPE Thermoplastic Elastomer
- SABIC Innovative Plastics Ultem LTX921A PEI Blend
- A. Schulman POLYFORT™ FPP 1842 Homopolymer Polypropylene
- Dow Corning CE 8401 EMULSION
- Dow Corning SC 102
- Diamond Polymers NPP25-1202 TF20 20% Talc Filled Copolymer Polypropylene, Impact Modified, High Heat, High Stiffness with UV and Paintable Versions
- Arlon CLTE-XT High Precision Ceramic PTFE
- 3M Scotch® 827 Pouch Tape
Copyright © lookpolymers.com All Rights Reserved