Diamond Polymers PC-1212FRO Natural, Flame Retardant Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers PC-1212FRO Natural, Flame Retardant Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 59.0 MPa
8560 psi
chs 2.0 in/min; ASTM D638
Tensile Strength, Yield 62.0 MPa
8990 psi
chs 2.0 in/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
chs 0.05 in/min; ASTM D790
Flexural Modulus 2.277 GPa
330.3 ksi
chs 0.05 in/min; ASTM D790
Izod Impact, Notched 6.48 J/cm

@Thickness 3.17 mm
 12.1 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 137 °C
279 °F
0.125";; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
0.125";; ASTM D648
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0620 in
5VA

@Thickness 3.17 mm
 5VA

@Thickness 0.125 in