Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 7606 GRAPHITE The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 1.3 g/10 min @Temperature 190 °C |
1.3 g/10 min @Temperature 374 °F |
|
North Wood Plastics 60 PP + UNIFILL (20% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips 5554-D LDPE High Clarity, Medium Impact, Low Slip Film Resin
(discontinued **) Resin Type: HomopolymerCharacteristics: Excellent Clarity, Good Impact Strength, Good Sealability, Low SlipApplications:Food Packaging, Case Shrink Wrap, LaminationsProcessing Conditions: Extruder 6.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 4003 Anhydride-Modified HDPE Adhesive Resin
(discontinued **) Bynel® Series 4000 resins are anhydride-modified, high-density polyethylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
ExxonMobil Escorene® LD-325 EVA Film Resin, High Clarity, High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.8% vinyl acetate copolymer, high clarity film resin. The combination of low melt index and comonomer content helps produce films which exhibit .. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Huntsman PE 1402 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell SEQUEL® E3000 TPO Description: SEQUEL® E3000 thermoplastic olefinic elastomer (TPO) is designed for thermoformed exterior and interior applications that require toughness and dimensional stability. This extrusion.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Hyosung Topilene F301U PP F301U Extrusion General HomopolymerApplications: Heavy duty bagCharacteristics:ProcessabilityWeatherabilityHigh tenacityInformation provided by Hyosung Corporation |
|||
Melt Flow | 1.3 - 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 - 1.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 0133 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® NA814000 Low Density Polyethylene ApplicationsPETROTHENE NA 814-000 is a low density homopolymer resin specifically developed for a wide variety of blow molding applications. This resin exhibits excellent gloss, an excellent balanc.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Solvay Specialty Polymers Polidiemme® G/420 Thermoset Elastomer (TSE) Polidiemme® XLPO -Cross-linkable Polyolefin. Elastomer based compound crosslinkable by ambient moisture, consisting of a silane pregrafted base compound to be used with a catalyst masterbatch (Si.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Shuman 210 Polyphenylene Ether Copolymer Alloy Black, Custom Colors. Good impact strength, easy processability, good chemical resistance, injection molding and extrusion grades.Data provided by the manufacturer. |
|||
Melt Flow | 1.3 g/10 min @Load 5.00 kg, Temperature 260 °C |
1.3 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP (Asia Pacific) 40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12 Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Condition 190/2.16; ASTM D1238 |
Chevron Phillips MarFlex® D143 m-LLDPE Linear Low Density Polyethylene Low Density PolyethyleneCustomer Benefits: This metallocene LLDPE film resin possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved proce.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
Chevron Phillips Marlex® 5104 LDPE Blow Molding Resin Resin Type: HomopolymerCharacteristics: High Melt Strength, Good Parison Control, Good Stability, Low Taste and Odor Characteristics, Good Impact and Toughness, Good Clarity on Gloss, Long Standing .. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ExxonMobil Method |
ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications Product Description: Exact 3128 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. It is designed fro both monolayer and multilayer coextruded .. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Exceed™ 1327CA Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1327CA is a metallocene ethylene-hexene copolymers. It produces films which have high modulus whilst retaining good toughness. These properties together with excellent dr.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Exceed™ 1327KD Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1327KD is a metallocene ethylene-hexene copolymer. It produces films which have high modulus whilst retaining good toughness. Additionally, Exceed 1327KD is fully formula.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1601-2 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 1601-2 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, s.. |
|||
Melt Flow | 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Diamond Polymers ABS 9950 Injection Molding Grade Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Orgalloy® RS 6015 EST Nylon 6 Alloy, 18% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties... |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
Braskem PRB 0131 RACO Random Polypropylene Copolymer PRB 0131 is a low melt flow rate random copolymer with high transparency. This resin is designed for thermoforming, blow molding, and extrusion. This product exhibits excellent processability, low h.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Carmel Olefins CAPILENE® SE 50 E Polypropylene Impact Copolymer Description: CAPILENE® SE 50 E is a low melt flow rate impact copolymer intended for sheet extrusion. It exhibits excellent impact strength even at low temperatures, combined with good processabi.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact Information provided by Asahi Thermofil |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact stren.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ISO 1133 |
Lucite International Diakon® ST45G8 Toughened Acrylic Polymer The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the Diakon® series can be processed by in.. |
|||
Melt Flow | 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Styron PULSE™ EXT 100 PC/ABS Engineering Resin Overview: PULSE EXT 100 engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE EXT 100 engin.. |