SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0017 - 0.0018 cm/cm @Thickness 3.20 mm |
0.0017 - 0.0018 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0027 - 0.0061 cm/cm @Thickness 3.20 mm |
0.0027 - 0.0061 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.3 g/10 min @Load 5.00 kg, Temperature 260 °C |
1.3 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 6.4 % | 6.4 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.31 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -30.0 °C |
1.80 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.76 J/cm | 10.8 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 14.0 J @Temperature -30.0 °C |
10.3 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C @Thickness 3.20 mm |
295 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 163 °C | 325 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A Zip 22 Natural Polyamide 66 (Nylon 66)
- LATI Latene® 7H2W T-V0 PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant
- Mitsui LUCANTâ„¢ HC-10 Synthetic Oil
- A. Schulman POLYBATCH™ Grey 8035 Concentrate Based In Polyethylene
- Goodfellow Platinum 70/Rhodium 30 Thermocouple Alloy
- Chengdu Polyster CH4132 Thermoplastic Polyether-ester Elastomer (TPEE)
- CoorsTek Superstrate® 996 99.6% Alumina Thin Film
- Dow 221.00 Developmental Performance Polypropylene Polymer
- Eurotec® Tecomid® NB40 GR30 NL AX70 PA6, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- 3M 1126 EMI Shielding Tape
Copyright © lookpolymers.com All Rights Reserved