| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 4.34 GPa | 630 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | ASTM D648 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 80 PHR Dixie Clay Filler
- LATI Latishield 36/AR-08A G/17-V0E ABS, Steel/Glass Fiber Reinforced, Flame Retardant
- SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East)
- Techmer ES Plaslube® J-50/10/TF/10 Polycarbonate, 10% GFR, 10% PTFE
- Solvay Specialty Polymers Algoflon® L203 Polytetrafluoroethylene (PTFE)
- Loctite® 641 Controlled Strength Retaining Compound
- ExxonMobil HDPE HTA 001HP2 High Density Polyethylene (HMW) Resin
- Arkema Group OREVAC® 18910 Maleic Anhydride Modified Copolymer
- Arlon R30082R012 0.012" (0.305 mm) Cured Silicone Rubber with Fiberglass Substrate
- Alliance Polymers Viprene™ P50A-22U-BLK Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved