LyondellBasell SEQUEL® E3000 TPO
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | SEQUEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell SEQUEL® E3000 TPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SEQUEL® E3000 thermoplastic olefinic elastomer (TPO) is designed for thermoformed exterior and interior applications that require toughness and dimensional stability. This extrusion-grade material is readily processed into a variety of products and has excellent chemical resistance. This material can be supplied with or without UV stabilizers. Applications: Sheet extrusion and thermoforming Information provided by Solvay Engineered Polymers.LyondellBasell acquired Solvay Engineered Polymers in 2008.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 275 % | 275 % | ASTM D638 |
| Flexural Modulus | 2.069 GPa | 300.1 ksi | I.B., TAN, 0.5 in/min; ASTM D790 |
| Izod Impact, Notched | 9.88 J/cm | 18.5 ft-lb/in | NB; ASTM D256 |
| 1.66 J/cm @Temperature -30.0 °C |
3.10 ft-lb/in @Temperature -22.0 °F |
PB; ASTM D256 | |
| Gardner Impact | 35.0 J @Temperature -30.0 °C |
25.8 ft-lb @Temperature -22.0 °F |
ASTM D5420-96 |
| >= 36.2 J @Temperature 23.0 °C |
>= 26.7 ft-lb @Temperature 73.4 °F |
ASTM D5420-96 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.1 µm/m-°C @Temperature 20.0 °C |
26.7 µin/in-°F @Temperature 68.0 °F |
modified; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | all colors |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G60S FFKM White Perfluoroelastomer
- ICO Polymers ICORENEâ„¢ 195-4060 LMDPE Rotational Molding Resin
- LG Chemical SEETEC M1315 Polypropylene Impact Copolymer
- Henkel Frekote PMC Mold Solvent
- Solvay TECHNYL® A 218G2 V30 Black 34N PA66, 30% glass fiber, Conditioned
- SABIC Innovative Plastics LNP STAT-KON DE0029 PC
- SABIC Innovative Plastics LNP STAT-KON RE004 PA 66
- Styrolution Novodur® H950 ABS
- TSE Industries Millathane® 66 Millable Polyurethane Rubber
Copyright © lookpolymers.com All Rights Reserved