Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® BD 30 Low Density Polyethylene - Blow Molding Riblene BD 30 is a low density polyethylene resin (LDPE) characterized by high melt strength and optimum processability.Parts manufactured with Riblene BD 30 have good mechanical performances.Main A.. |
|||
Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Network Polymers MS 100 Styrene Methyl Methacrylate Copolymer Description: Styrene Methyl Methacrylate CopolymerInformation provided by Network Polymers Inc. |
|||
Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Network Polymers MS 110 Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
NOVA Chemicals Dylark® 378P15 Glass Reinforced Engineering Resin Features: Very high modulus, High heat resistance, excellent flow characteristics, excellent adhesion to urethaneApplications: Instrument panel substrates, Consoles, Cluster housings, Interior trim |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® HE-Y449-A HDPE Extrusion Resin Features: High ESCR, good toughness, good chemical resistance, good processability.Applications: Pipe coatings, profile extrusions, sheet extrusion for thermoforming, corrugated tubing, conduit.Data.. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 220 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 428 °F |
ISO 1133 |
DuPont Performance Polymers Hytrel® HTR237BG BK320 TPC-ET
(Unverified Data**) Hytrel® HTR237BG is designed for blow molding or processing techniques requiring high viscosity. It has nominal durometer hardness of 45D, is pigmented black with fine particle size carbon black an.. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
NOVA Chemicals Dylark® 480P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp.. |
|||
Melt Flow | 0.40 - 0.70 g/10 min | 0.40 - 0.70 g/10 min | |
Kazanorgsintez 102-57 Low Density Polyethylene Composite, for Further Radiation Modification Production Method: Composition is produced on the basis of 10204-003 base grade low density polyethylene or first and primary grades. Application: Used for heat and radiation resistant wires and.. |
|||
Melt Flow | 0.40 - 0.65 g/10 min | 0.40 - 0.65 g/10 min | ±10% Superior Class, ±18% 1st Class |
Kazanorgsintez 273-83 High Density Polyethylene Composite Production Method: Gaseous-phase method. Application: Composition of HD grade 273-83 is intended to obtain by method of extrusion products of industrial, cultural, and general use as well as goo.. |
|||
Melt Flow | 0.40 - 0.70 g/10 min | 0.40 - 0.70 g/10 min | ±18% |
Kazanorgsintez 293-285 High Density Polyethylene Composite, Film Grade Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions are .. |
|||
Melt Flow | 0.40 - 0.75 g/10 min | 0.40 - 0.75 g/10 min | ±18% |
Kazanorgsintez 297-285 High Density Polyethylene Composite Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions 296-.. |
|||
Melt Flow | 0.40 - 0.80 g/10 min | 0.40 - 0.80 g/10 min | ±10% |
Kazanorgsintez PE80B-285 High Density Polyethylene Composite, Film Grade Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions are .. |
|||
Melt Flow | 0.40 - 0.80 g/10 min | 0.40 - 0.80 g/10 min | ±10% |
Kazanorgsintez PE80B-285D High Density Polyethylene Composite, Film Grade Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions are .. |
|||
Melt Flow | 0.40 - 0.80 g/10 min | 0.40 - 0.80 g/10 min | ±10% |
Kazanorgsintez PE80B-285SL High Density Polyethylene Composite, Film Grade Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions are .. |
|||
Melt Flow | 0.40 g/10 min | 0.40 g/10 min | ASTM D1238 |
Hyosung Topilene B240 PP B240 Extrusion Impact CopolymerApplications:Corrugated sheetThick sheetCharacteristics:High impactInformation provided by Hyosung Corporation |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical LUTENE FB0300 LDPE Blown Film Grade Description: LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the e.. |
|||
Melt Flow | 0.40 - 0.70 g/10 min | 0.40 - 0.70 g/10 min | ±18% |
Kazanorgsintez 293-285SK High Density Polyethylene Composite, Film Grade Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions are .. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 1125 AC Ethylene and 25% Methyl Acrylate Copolymer Elvaloy® 1125 AC is intended for coextrusion and molding. It can be recommended for blow molding of parts requiring permanent flexibility, stress cracking resistance and softness. Excellent fill.. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total EVA 1003 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1003 VN 4 is made by a high pressure tubular process. Grade for flexible films with very high transparency and outstanding mechanical properties. Contains an antioxidant.Application examples: .. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Total L425 HDPE Film Blown film polyethylene grade. Provides excellent bubble stability, exceptional tear strength, high impact and puncture resistance, outstanding clarity and gloss, good stiffness, excellent compatibi.. |
|||
Melt Flow | 0.40 g/10 min | 0.40 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips MarFlex® 5619 LDPE Shrink and Heavy Duty Packaging Film Resin Resin Type: HomopolymerCharacteristics: Excellent Tensile and Impact Strength, Good Abrasion and Tear Resistance, Good Resistance to Blocking, Wide Range of Shrinkage Characteristics, Low Slip, Low .. |
|||
Melt Flow | 0.40 - 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 - 1.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Diamond Polymers ABS 9401 Injection Molding Grade, Ultra High Impact Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 0.40 - 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 - 1.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Diamond Polymers ABS 9501 Description: Injection Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg |
0.40 g/10 min @Load 4.76 lb |
ASTM D1238 |
Equate EMDA-6200 HDPE Blow Molding Resin EMDA-6200 grade is a high-density polyethylene copolymer resin designed for blow molding small to medium size bottles. It can be used on intermittent as well as continuous blow molding machines for .. |
|||
Melt Flow | 0.40 g/10 min | 0.40 g/10 min | ASTM D1238 |
Aclo Accutech ABS ABS832G30L Glass Reinforced |
|||
Melt Flow | 0.40 - 0.70 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.40 - 0.70 g/10 min @Load 11.0 lb, Temperature 374 °F |
UNI EN ISO 1133 |
Breplast Bretene TST High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 0.40 g/10 min | 0.40 g/10 min | |
Ashley Polymers Ashlene® ABS Resin F-217 General purpose super high impact with good gloss.Data provided by the manufacturer |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® HB-L455-A HDPE Blow Molding Resin
(discontinued **) Molded Plaque Properties. Features: excellent processability on high speed, multiple-head blow molding lines, good balance of physical and molding properties.Applications: chemical bottles, toys.Da.. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Escorene™ LD 705.MJ Blown Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra LD 705.MJ is a fractional melt index, 12.8 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and.. |
|||
Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 99C HDPE Extrusion Resin
(discontinued **) Features: Excellent processability, excellent stretchability, high stiffness, superior strength, gel-free.Applications: Industrial woven bags, tarpaulins.Data provided by the manufacturer. |