Network Polymers MS 100 Styrene Methyl Methacrylate Copolymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Polystyrene (PS) , Styrene/Methyl Methacrylate Copolymer (SMMA) |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers MS 100 Styrene Methyl Methacrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Styrene Methyl Methacrylate CopolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.5 MPa | 9500 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | chs 2 in/min; ASTM D638 |
| Tensile Modulus | 3.45 GPa | 501 ksi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.16 GPa | 458 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.246 J/cm | 0.460 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C1110HF PC+ABS (Asia Pacific)
- Karina MBU Antiblock
- ICO Polymers ICORENEâ„¢ 155-1331 LMDPE Rotational Molding Resin
- Momentive Performance Materials RTV511 Silicone Rubber Compound for Low Temperature Potting, Encapsulating and Sealing, White
- Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant
- UBE PAE1201U Nylon Elastomer
- Cossa Polimeri ESTAPROP 1000 V2 K Flame Retardant Polypropylene
- Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding
- Aaron Industries AAROPRENE® CFPP 2030 Calcium Carbonate Filled Polypropylene
Copyright © lookpolymers.com All Rights Reserved