Total EVA 1003 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Total Atofina
Trade Name EVA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total EVA 1003 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EVA 1003 VN 4 is made by a high pressure tubular process. Grade for flexible films with very high transparency and outstanding mechanical properties. Contains an antioxidant.Application examples: High strength stretch film, greenhouse film, film for food packaging (coextrusion), stretch hood.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.935 g/cc
0.935 g/cc
ISO 1183
Vinyl Acetate Content 13.5 %
13.5 %
Thickness 40.0 microns
1.57 mil
for samples tested on this data sheet
30.0 - 300 microns
1.18 - 11.8 mil
possible range, depending on extrusion conditions
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 6.50 MPa
943 psi
ISO 527-3
Film Tensile Strength at Yield, TD 5.00 MPa
725 psi
ISO 527-3
Film Elongation at Break, MD 310 %
310 %
ISO 527-3
Film Elongation at Break, TD 590 %
590 %
ISO 527-3
Modulus of Elasticity 0.0700 GPa
10.2 ksi
ISO 527-2
Elmendorf Tear Strength, MD 1.30 g/micron
33.0 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.90 g/micron
73.7 g/mil
ISO 6383-2
Dart Drop Test 650 g
1.43 lb
ISO 7765-1
Film Tensile Strength at Break, MD 38.0 MPa
5510 psi
ISO 527-3
Film Tensile Strength at Break, TD 38.0 MPa
5510 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 92.0 °C
198 °F
ISO 11357
Vicat Softening Point 74.0 °C
165 °F
ISO 306
Optical Properties Metric English Comments
Haze 2.5 %
2.5 %
ISO 14782
Processing Properties Metric English Comments
Processing Temperature 150 - 180 °C
302 - 356 °F