DuPont Elvaloy® 1125 AC Ethylene and 25% Methyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 1125 AC Ethylene and 25% Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 1125 AC is intended for coextrusion and molding. It can be recommended for blow molding of parts requiring permanent flexibility, stress cracking resistance and softness. Excellent filler acceptance makes Elvaloy® 1125 AC suitable for highly filled compounds.Elvaloy® 1125 AC is easily processed on standard equipment used for low-density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 28 | 28 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 760 % | 760 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0250 GPa | 3.63 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 90.0 °C | 194 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 48.0 °C | 118 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MA-Content | 25 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- DSM Akulon® K224-HGR24 Nylon 6-30% Glass Fiber and Glass Bead Reinforced (European Grade) (Cond) (discontinue
- Lucas-Milhaupt BRAZE 505 Carbide Brazing Alloy
- Styron CALIBREâ„¢ 200 6 Polycarbonate, General Purpose
- SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East)
- ChevronTexaco 800 NC Open Gear Lubricant
- Epoxy Technology EPO-TEK® 375 High Temperature Epoxy
- Chosun Refractories CTL-VBC Monolithic Refractories for Ladle and Tundish
- CIMBAR CIMBAR™ PC Barite Powder (BaSO4)
- Arkema Group Nakan® RMA 705 N PVC, Rigid Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved