- Polymer Property : Melt Flow = 9.0 g/10 min
Polymer Property : Melt Flow = 9.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ PPH-10G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | |
| Nylene® Naxel™ PC10 Polycarbonate Description: Naxel™ PC10 is a 9 melt, general purpose polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources C.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products T40P100-04 40% Talc Reinforced Polypropylene, White Applications: Automotive componentsConsumer productsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| NCMT NanoPAC™ G3000 High Performance Polypropylene Nanocomposite Applications: Automobile Construction MaterialInformation provided by Nano Composite Materials Technology Limited |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Greenflex® MP 35 Ethylene Vinyl Acetate Copolymer - Injection Molding & Extrusion Greenflex MP 35 is an ethylene vinyl acetate copolymer (EVA) for injection molding and extrusion. Greenflex MP 35 is an easy flowing material and provides a very high elasticity.Main Applications: .. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A Condition E; ASTM D1238 |
| Network Polymers Kepital® F20-25 Description: Natural Acetal Copolymer, 25% Glass Reinforced GradeInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS (Asia Pacific) AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1183 |
| Pasargad Polymer Peyvand Pasalen 3P-H3520B Polypropylene, 20% EPDM Filled Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components BumperAutomotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad.. |
|||
| Melt Flow | 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 - 16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-UV2-D-[color]-1 Polycarbonate, UV-stabilized, Medium Flow with Mold Release Polycarbonate, UV-stabilized, Medium Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
|
| PTS POM-90 9.0 MFI Acetal Copolymer Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
|
| Ineos ABS Lustran® QE 1094 AS, Injection Grade
(discontinued **) Injection molding grade, super high impact.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under.. |
|||
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Kolon KOCETAL® EL304 Toughened Grade Acetal Resin Flexible grade. Applications: Flexible products. Information provided by API-Kolon. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| LyondellBasell Hostacomâ„¢ CB267 Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB267 medium melt flow, 1,600 MPa flexural modulus thermoplastic elastomeric olefin (TEO) resin has an excellent balance of scratch and mar resistance, rigidity and impac.. |
|||
| Melt Flow | 9.0 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.0 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| SABIC Innovative Plastics ULTEM 1000F PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 Listing. Effective June, 2007 this grade will no long.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber AvaSpire® AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 res.. |
|||
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| SPS Guang Zhou SAMATâ„¢ 168(f1) Flame-retarded Polypropylene Characteristic: Good flame resistance, good chemical resistance, good mechanical propertiesApplications: X'mas decorative product, E/E applianceInformation Provided by SPS (Guang Zhou) Ltd. |
|||
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL EXT115 PPE+PS (Asia Pacific) PPE+PS, Auto exterior grade, wax remover resistant |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Borealis Borstar® CB9600 HDPE for Extrusion Coating Borstar CB9600 is the first bimodal high-density coating grade produced using the unique Borstar PE technology. The process controls the polymer `s molecular structure and is designed to produce bi.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis Daplen™ ED117AE Polypropylene TPO Compound Daplen™ ED117AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and gives a good surfac.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer Elvaloy® 1913 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy®.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polyram RamTal PM1109 Acetal, General Purpose General purpose polyacetal copolymer for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polyram RamTal PM1419 Acetal, PTFE Filled Polyacetal filled with PTFE for sliding parts, low friction and improved wear resistance in molded parts.Information provided by Polyram Ram On Ind. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red LL50304/3 Concentrate Based In LLDPE DescriptionPOLYBATCH® LL50304/2 is a red color concentrate based in LLDPE. This concentrate was designed to provide opacity and color in blow molding applications. POLYBATCH® LL50304/2 is heavy .. |
|||
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | |
| Zeon Chemicals Quintac® 3620 SIS Block Polymer Styrene Isoprene (SIS) Block Polymer. Standard grade for hot melt PSAInformation provided by Zeon Chemicals L.P. |
|||
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Chevron Phillips K-Resin® KK38 Styrene-Butadiene Copolymer, Sheet Grade Styrene-Butadiene CopolymerCustomer Benefits: KK38 is an improved extrusion grade SBC designed specifically for superior performance in blends with general purpose polystyrene. It is easily process.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
| Braskem RP 344 RACO Random Polypropylene Copolymer RP 344 is a medium melt flow rate random copolymer. It is suitable for blown and cast film extrusion and features good processability, excellent optical properties, and outstanding sealability. Its .. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Azoty Tarnow™ TARNOFORM 300 GB4 POM 20% glass beads filled grade with increased stiffness and hardness with lowered shrinkageInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® EXL5689 PC Copolymer Lexan* EXL5689 polycarbonate (PC) resin is a GF reinforced, UV stabilized, flame retardant injection molding copolymer blend. This medium flow resin features UL94 V0 @ 1.5mm flame retardancy based .. |
|||
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| LG Chemical 15NFI GPPS High flow, Superior transparency and processability, good appearance, non-toxicity (Conforming to FDA CFR 177.1640), Excellent electrical properties, Heat resistance and chemical resistance, Superio.. |
|||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Gold 7060E POLYBATCH® Concentrate Based In LDPE Description POLYBATCH® 7060E is a gold color concentrate based in LDPE. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 7060E is heavy meta.. |
|||