- DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer
DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 1913 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy® 1913 AC is easily processed on standard equipment used for low density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 760 % | 760 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0650 GPa | 9.43 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 98.0 °C | 208 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 60.0 °C | 140 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MA-Content | 13 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Honeywell Aegisâ„¢ H135QP Nylon 6 Extrusion Grade Homopolymer Film
- Lendell NolaSponge®
- Teknor Apex Telcar® TL-1425A Thermoplastic Elastomer
- Hexcel® HexWeb® HRH-327 - 3/8 - 4.0 Fiberglass Reinforced Polyimide Honeycomb
- DSM Akulon® K222-D Nylon 6 (European and Asian Grade) (Dry)
- Eurostar Starpylen HU 70E4 ECR
- Bulk Molding Compounds BMC 605L Mineral Filled, Glass Fiber Reinforced Polyester Compound
- Alliance BIN-55 Bonded (Composite) Magnetic Material
- AK Steel CARLITE® M-6 Grain Oriented Electrical Steel (Extended Electro-Magnetic Data)
- PolyOne Elastamax XL 1092-35 TPU-Based Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved