Samsung Cheil Industries Infino® CF-1050 PC, Unreinforced High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® CF-1050 PC, Unreinforced High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 250 °C |
20 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 7.35 J/cm @Thickness 3.17 mm |
13.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 143 °C | 289 °F | B/50; ISO R306 |
| Flammability, UL94 | V-2 @Thickness 0.800 - 3.00 mm |
V-2 @Thickness 0.0315 - 0.118 in |