SABIC Innovative Plastics Xenoy® XD1607 PBT+PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® XD1607 PBT+PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
22% Glass filled PBT+PC with a designed balance between surface appearance and mechanical properties sufficient for automotive doorhandle requirements. Special suitable for gas assist mouldings .This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
0.50 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on tensile bar; SABIC Method
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 250 °C
11 g/10 min

@Load 11.0 lb,
Temperature 482 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 115 MPa
16700 psi
ISO 2039-1
Tensile Strength at Break 110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 7.00 GPa
1020 ksi
1 mm/min; ISO 527
Flexural Strength 165 MPa
23900 psi
2 mm/min; ISO 178
Flexural Modulus 6.50 GPa
943 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Taber Abrasion, mg/1000 Cycles 30

@Load 1.00 kg
30

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.180 W/m-K
1.25 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 126 °C
259 °F
Rate B/50; ISO 306
130 °C
266 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
3.3

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2