SABIC Innovative Plastics ULTEM SF2250 PEI Blend
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM SF2250 PEI Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Ultem for thin wall application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH |
| Linear Mold Shrinkage, Flow | 0.0046 cm/cm | 0.0046 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0054 cm/cm | 0.0054 in/in | SABIC Method |
| Melt Flow | 19.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
19.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 40 g/10 min @Load 10.0 kg, Temperature 345 °C |
40 g/10 min @Load 22.0 lb, Temperature 653 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 157 MPa | 22800 psi | 5 mm/min; ISO 527 |
| 162 MPa | 23500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.90 GPa | 1290 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 197 MPa | 28600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.15 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| 7.26 GPa | 1050 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.890 J/cm | 1.67 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -40.0 - 150 °C |
7.78 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 18.0 µm/m-°C @Temperature 23.0 - 150 °C |
10.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 59.0 µm/m-°C @Temperature 23.0 - 150 °C |
32.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Rogers Corporation TMM® TMM3 Ceramic Thermoset Polymer Composite
- Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced
- Nilit FRIANYL A63 N-SG5 Nylon 6.6 for injection molding, 5% mineral filled
- Polymer Resources TP-IM-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Impact Modified
- Momentive Performance Materials RTV627 Dark Gray General Purpose Potting/Encapsulating Compound
- Shakespeare Isocorâ„¢ 651 Nylon 6 Terpolymer
- Plastics Group Polifil® 627L Nylon 6/6 (DAM)
- Chosun Refractories GUN-140L Light-Weight Gunning Castable
- Ashley Polymers Ashlene® 745 Nylon 6/69
- BASF Ultradur® B 4300 K6 30% Glass Bead Filled PBT
Copyright © lookpolymers.com All Rights Reserved