Polymer Property : Melt Index of Compound = 40 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 220 °C	40 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Cycolac® FR15U ABS Flame retardant ABS with excellent indoor UV properties and excellent processing. UL94 V-0/5VA rated. Elevated UL RTI rating (90-85-90) for all colors except for blue and green colors (60-60-60).
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 220 °C	40 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific) Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94 V-0/5VA rated.ing.
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 220 °C	40 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Cycolac® FR15U ABS (Europe-Africa-Middle East) CYCOLAC FR15U is a flame retardant ABS with good processability and good indoor UV properties.
Melt Index of Compound	40 g/10 min @Load 5.00 kg, Temperature 260 °C	40 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133
Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized Information provided by Polykemi AB
Melt Index of Compound	40 g/10 min @Load 5.00 kg, Temperature 265 °C	40 g/10 min @Load 11.0 lb, Temperature 509 °F	ASTM D1238
3M Dyneon™ THV 340C Fluorothermoplastic (discontinued **) THV 340C is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of concentrated water-based dispersion containing an ionic..
Melt Index of Compound	40 g/10 min	40 g/10 min	ASTM D1238
LG Chemical AT-553 Transparent ABS, Permanent Antistatic, Natural and Colored Pellets LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electron..
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 210 Â°C	40 g/10 min @Load 22.0 lb, Temperature 410 Â°F	cm<sup>3</sup>/10 min
Huntsman IROGRANÂ® A 92 E 4738 Polyester-Based TPU-Injection Extrusion Grade Introduction: IROGRAN A 92 E 4738 is a white-colored, thermoplastic special-polyester-polyurethane for injection molding applications. Additional characteristics of the product are flexibility and h..
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 345 Â°C	40 g/10 min @Load 22.0 lb, Temperature 653 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM SF2250 PEI Blend (Asia Pacific) High flow Ultem for thin wall application
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 345 Â°C	40 g/10 min @Load 22.0 lb, Temperature 653 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific) High flow Ultem for thin wall application
Melt Index of Compound	40 g/10 min @Load 2.16 kg, Temperature 250 Â°C	40 g/10 min @Load 4.76 lb, Temperature 482 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ValoxÂ® SHF4340 PBT (Europe-Africa-Middle East) 20% GF Super High Flow PBT
Melt Index of Compound	40 - 48 g/10 min @Load 2.16 kg, Temperature 240 Â°C	40 - 48 g/10 min @Load 4.76 lb, Temperature 464 Â°F	ASTM D1238
Shinkong Synthetic Fibers ShiniteÂ® D201K002 PBT, Low Viscosity Information from Shinkong Synthetic Fibers Corp.
Melt Index of Compound	40 g/10 min @Load 21.6 kg, Temperature 300 Â°C	40 g/10 min @Load 47.6 lb, Temperature 572 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL HH180 PPE+PS Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Melt Index of Compound	40 g/10 min @Load 21.6 kg, Temperature 300 Â°C	40 g/10 min @Load 47.6 lb, Temperature 572 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL HH180 PPE+PS (Asia Pacific) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Melt Index of Compound	40 g/10 min @Load 21.6 kg, Temperature 300 Â°C	40 g/10 min @Load 47.6 lb, Temperature 572 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL HH180 PPE+PS (Europe-Africa-Middle East) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Melt Index of Compound	40 g/10 min @Load 10.0 kg, Temperature 345 Â°C	40 g/10 min @Load 22.0 lb, Temperature 653 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM SF2250 PEI Blend High flow Ultem for thin wall application
Melt Index of Compound	40 g/10 min @Load 2.16 kg, Temperature 250 Â°C	40 g/10 min @Load 4.76 lb, Temperature 482 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ValoxÂ® SHF4340 PBT 20% GF Super High Flow PBT
Melt Index of Compound	40 - 48 g/10 min @Load 2.16 kg, Temperature 240 Â°C	40 - 48 g/10 min @Load 4.76 lb, Temperature 464 Â°F	ASTM D1238
Shinkong Synthetic Fibers ShiniteÂ® D201K002 PBT, Low Viscosity Information from Shinkong Synthetic Fibers Corp.
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..
Melt Index of Compound	40 g/10 min @Load 2.16 kg, Temperature 190 °C	40 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group LOTADER® 6200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 6200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 62..
Melt Index of Compound	40 g/10 min	40 g/10 min	Condition E; ASTM D1238
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo..