SABIC Innovative Plastics LNP THERMOCOMP JF006LZZ PES

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP JF006LZZ PES.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* JF006LZZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Extrusion Grade, Low Extractable.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
1.613 g/cc
0.05827 lb/in³
ASTM D792
Moisture Absorption 0.360 %
0.360 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Time 86400 sec
0.0020 in/in

@Time 24.0 hour
ASTM D955
0.0025 cm/cm

@Time 86400 sec
0.0025 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0069 cm/cm

@Time 86400 sec
0.0069 in/in

@Time 24.0 hour
ISO 294
0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 99.0 MPa
14400 psi
ISO 527
113 MPa
16400 psi
ASTM D638
Elongation at Break 1.4 %
1.4 %
ISO 527
1.8 %
1.8 %
ASTM D638
Tensile Modulus 9.79 GPa
1420 ksi
50 mm/min; ASTM D638
10.19 GPa
1478 ksi
1 mm/min; ISO 527
Flexural Strength 178 MPa
25800 psi
ASTM D790
222 MPa
32200 psi
ISO 178
Flexural Modulus 9.23 GPa
1340 ksi
ASTM D790
9.24 GPa
1340 ksi
ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.32 J/cm
8.09 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 12.0 J
8.85 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
30.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 36.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
36.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 217 °C

@Thickness 3.20 mm
423 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 212 °C

@Thickness 3.20 mm
414 °F

@Thickness 0.126 in
unannealed; ASTM D648