- SABIC Innovative Plastics LNP STAT-KON TX06488NTX1 PU
SABIC Innovative Plastics LNP STAT-KON TX06488NTX1 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON TX06488NTX1 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* TX06488NTX1 is a compound based on Polyurethane resin containing Proprietary Filler(s). Added features of this grade are: Execllent Ductility, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.670 % | 0.670 % | 50% RH, 24 hrs; ASTM D570 |
| 0.890 % | 0.890 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 392 % | 392 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 388 % | 388 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 0.0600 GPa | 8.70 ksi | 5 mm/min; ASTM D638 |
| Flexural Modulus | 0.0600 GPa | 8.70 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Dart Drop, Total Energy | 39.0 J @Temperature 23.0 °C |
28.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 41.0 J | 30.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 23.0 °C | 73.4 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 23.0 °C @Thickness 3.20 mm |
73.4 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 23.0 °C | 73.4 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 23.0 °C @Thickness 3.20 mm |
73.4 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Fluorosint® HPV PTFE + additives, bearing grade, compression moulded (ISO Data)
- Huntsman PE5080 Extrusion Coating Polyethylene (discontinued **)
- Kinlead PG12 Bag Grade BOPP Plain Film (thickness: 30 µm)
- Lord Adhesives Aeroglaze® K3425 Sandable Primer/Surfacer
- Solvay TECHNYL® C 52G1 V25 Grey R7035 (XC 1329/A) PA6, DRY
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
- Dow Corning 3580 Performance Modifier
- Ametek High Purity Nickel Strip 899A Skin Hard
- Lucas-Milhaupt HANDY HI-TEMP 095 Carbide Brazing Alloy
- Ashley Polymers Ashlene® PE128 PET Polyester, 45% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved