Plastics Group Polifil® RMT-10 10% Talc-Reinforced Polypropylene, High Impact

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer The Plastics Group of America
Trade Name Polifil®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastics Group Polifil® RMT-10 10% Talc-Reinforced Polypropylene, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polifil® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resistance. These compounds are used in automotive applications and conform to the requirements of the FMVSS-302. Standard processing techniques are applicable.Information provided by The Plastics Group.
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
ASTM D792
Filler Content 10 %
10 %
ASTM D2584
Linear Mold Shrinkage 0.013 cm/cm

@Thickness 1.59 mm
0.013 in/in

@Thickness 0.0625 in
ASTM D955
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
230/2.16; May be specified; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 87
87
ASTM D785
Tensile Strength at Break 29.48 MPa
4275 psi
ASTM D638
Flexural Modulus 1.83 GPa
265 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.854 J/cm
1.60 ft-lb/in
At 73°F; ASTM D256
Izod Impact, Unnotched 9.61 J/cm
18.0 ft-lb/in
At 73°F; ASTM D256
Gardner Impact 5.536 J
4.083 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
236 °F
ASTM D648