Polymer Property : Tensile Strength, Yield = 24500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	169 MPa	24500 psi	ASTM D638
PolyOne LubriOne™ NL-30CF/15T Black Polyamide 612 (Nylon 612) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength, Yield	169 MPa	24500 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne
Tensile Strength, Yield	169 MPa	24500 psi	50 mm/min; ASTM D638
Ovation Polymers UTTAP SF 50030GF Polyethersulfone, 30% Glass Reinforced Glass reinforced (30 %) Polyether Sulfone, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50%..
Tensile Strength, Yield	169 MPa	24500 psi	50 mm/min; ASTM D638
Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber Excellent chemical and electrical resistance, high stiffness, modulus and HDTAll properties after 48hrs conditioning at 23°C/50% RH
Tensile Strength, Yield	169 MPa	24500 psi	ASTM D638
GEHR Plastics Ultem 2300 PEI-30 GF 30% Glass Fiber Reinforced (discontinued **) Polyetherimide has a high mechanical strength in connection with a good chemical and heat resistance, good dimensional stability and great resistance. It's unique torque strength permits the econom..
Tensile Strength, Yield	169 MPa @Strain 0.200 %, Temperature 982 Â°C	24500 psi @Strain 0.200 %, Temperature 1800 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Yield	169 MPa	24500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66 LNP* LUBRICOMP* RFG16S is a compound based on Nylon 66 resin containing 5% Graphite, 30% Glass Fiber. Added features of this material include: Heat Stabilized, Wear Resistant.
Tensile Strength, Yield	169 MPa	24500 psi	ASTM D638
Techmer ES HiFillÂ® PA6 GF33 UG HS BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: General Purpose, Lubricated and Heat S..
Tensile Strength, Yield	169 MPa	24500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON REL33 PA 66 LNP STAT-KON* REL33 is a compound based on Nylon 66 resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.
Tensile Strength, Yield	169 MPa	24500 psi	ASTM D638
Techmer ES HiFillÂ® PPS GF40 TL13 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Tensile Strength, Yield	169 MPa	24500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing Glass Fiber.
Tensile Strength, Yield	169 MPa	24500 psi	ASTM D638
Ashley Polymers Ashlene® 990L-40G Nylon 610, 40% Glass Reinforced 40% glass reinforced, excellent dimensional stability and low water absorption. Also available as: 990LS-40G, same with heat stabilizer.Data provided by the manufacturer
Tensile Strength, Yield	169 MPa	24500 psi	.0275 - .035 inches sheet thickness; ASTM A 370
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade Interstitial Free (I-F) steels are made by adding titanium to the molten steel after degassing and offer excellent drawability.Information provided by AK Steel