NOVA Chemicals Surpass® FPs317-A Octene sLLDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® FPs317-A Octene sLLDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Exceptional puncture resistanceVery good tear propertiesLow gel levelExcellent optical properties Excellent elongation characteristics Easy to process, no drying required Applications: Cast stretch wrap Co-extrusion and laminationInformation provided by Nova Chemicals
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D792
Thickness 20.0 microns
0.787 mil
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.52 MPa
1090 psi
ASTM D882
Film Tensile Strength at Yield, TD 7.03 MPa
1020 psi
ASTM D882
Film Elongation at Yield, MD 470 %
470 %
ASTM D638
Film Elongation at Yield, TD 780 %
780 %
ASTM D882
Elongation at Break 360 %
360 %
Puncture Energy 1.66 J
1.22 ft-lb
Low Friction Puncture
Elmendorf Tear Strength MD 375 g
375 g
ASTM D1922
Elmendorf Tear Strength TD 535 g
535 g
ASTM D1922
Film Tensile Strength at Break, MD 32.0 MPa
4640 psi
ASTM D882
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ASTM D882
1% Secant Modulus, MD 100 MPa
14500 psi
ASTM D882
1% Secant Modulus, TD 120 MPa
17400 psi
ASTM D882
Optical Properties Metric English Comments
Haze 0.80 %
0.80 %
ASTM D1003
Gloss 85 %
85 %
at 45°; ASTM D2457