NOVA Chemicals Novapol® LF-Y824-C LDPE Clarity Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® LF-Y824-C LDPE Clarity Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: High optical clarityExcellent processabilityExcellent shrink film characteristics Applications: High clarity shrink filmProduce and bakery filmTextile packaging filmInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.924 g/cc	0.0334 lb/in³	ASTM D792
Thickness	38.0 microns	1.50 mil
Melt Flow	0.75 g/10 min @Load 2.16 kg, Temperature 190 °C	0.75 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.5 MPa	1670 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.5 MPa	1670 psi	ASTM D882
Film Elongation at Yield, MD	350 %	350 %	ASTM D882
Film Elongation at Yield, TD	535 %	535 %	ASTM D882
Coefficient of Friction	>= 0.40	>= 0.40	ASTM D1894
Elmendorf Tear Strength MD	200 g	200 g	ASTM D1922
Elmendorf Tear Strength TD	290 g	290 g	ASTM D1922
Dart Drop Test	107 g	0.236 lb	F<sub>50</sub>; ASTM D1709/A
Film Tensile Strength at Break, MD	24.0 MPa	3480 psi	ASTM D882
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
1% Secant Modulus, MD	210 MPa	30500 psi	ASTM D882
1% Secant Modulus, TD	230 MPa	33300 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	6.0 %	6.0 %	ASTM D1003
Gloss	75 %	75 %	at 45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified