Polymer Property : Film Tensile Strength at Break, TD = 2900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527-3
Polimeri Europa Riblene® FM 23 Low Density Polyethylene - Blown Film Extrusion Riblene FM 23 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FM 23 is characterized by a good balance between processabilit..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PS 1324 PRE-ELEC PS 1324 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Petroquimica Triunfo Trithene® TS 7010 LDPE - Medium Duty Packaging The Trithene TS 7010 resin is a low-density polyethylene (LDPE) with a high molecular weight, excellent processability, and good mechanical properties. The incorporated additives package warrants th..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527-3
Polimeri Europa Clearflex® CL B0 Very Low Density Polyethylene Clearflex CL B0 is a linear low density polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin has a high stretchability and a good cling effect.Main Applications: C..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
M. Holland Company MAGMA® LL1091-K LLDPE (discontinued **) Features: Good Heat Seal, Good Processability, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland.
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA443023 Blown Low Density Polyethylene ApplicationsPETROTHENE NA 443 is a series of low density/EVA copolymer resins for high impact/high clarity packaging applications. NA 443 exhibits excellent processability and good balance of optic..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527-3
Borealis Himod™ FT6273 LDPE for Film Himod FT6273 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Westlake EF603 Low Density Polyethylene Westlake EF603 is a LDPE resin with excellent toughness and processability. It is suggested in heavy duty films and medium duty shrink applications. It can be used as a bubble stabilizer in LLDPE ri..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Westlake Hifor Xtreme SC74840 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74840 linear low density polyethylene is recommended for the core layer of cast stretch film. It provides excellent clarity and ultimate stretch values higher than the more c..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527-3
Total LDPE 1022 FH 24 Low Density Polyethylene - Blown Film LDPE 1022 FH 24 is a low density polyethylene made by a high pressure process.LDPE 1022 FH 24 is a slip and anti-block formulated grade.LDPE 1022 FH 24 is suited to many applications in the field of..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Chevron Phillips MarFlex® 7109DJ LLDPE Blown Film Resin Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Dow INTEGRAL™ 900 Deep Draw Multilayer Adhesive Film INTEGRAL 900 Adhesive Film is a heat-activated, moldable, thermally stable adhesive film capable of bonding to urethane foam-baked fabrics, polyester and nylon fabrics, fiberglass, and rigid urethan..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Braskem CX7020 Cast Film Extrusion Low Density Polyethylene Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination, Injection-Blow Molding, Foamed applications.Information provided by Braskem.
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem CX7020 LDPE Cast Film Extrusion Polyethylene CX7020 is a low-density polyethylene (LDPE) with excellent processability and low gel content. Those features allow for production of thin and highly uniform films. This product is identified as PE ..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Braskem EB861/51 Blown Film Extrusion Low Density Polyethylene Film for general use; Shrink films; Coextrusion.Additives: Antiblock, DInformation provided by Braskem.
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem F 7018 LDPE Extrusion Coating Polyethylene LDPE F 7018 is a low-density polyethylene and has excellent processability and sealability at low temperatures. It does not contain additives. Its applications include: extrusion coating; and injec..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Braskem F0421D Blown Film Extrusion Low Density Polyethylene Shrink films; Automatic packaging of liquid products (FFS).Additives: Antiblock, DInformation provided by Braskem.
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem F2022/0 LDPE Cast Film Extrusion Polyethylene LDPE F2022/0 has excellent sealing characteristics and optical properties with well balanced mechanical properties. Its applications include: general purpose which require no additives; shrink film..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem F7018 LDPE Injection Molding Polyethylene F7018 is a low-density polyethylene with excellent processability and sealability at low temperatures. It does not contain additives. Its applications include: extrusion coating, injection molding ..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem FG31D LLDPE Blown Film Extrusion Polyethylene Copolymer The FG31D resin is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process for blow film extrusion in blends with polyethylene. It has excellent mechanical propert..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem FH35 HDPE Cast Film Extrusion Polyethylene Copolymer The FH35 resin is a high-density polyethylene, copolymer of butene-1, produced by the solution process for flat die film extrusion with good mechanical properties. It contains antioxidant additives...
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem FM31D LLDPE Blown Film Extrusion Polyethylene Copolymer The FM31D resin is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process for blown film extrusion. It has excellent mechanical properties, especially hot tack. I..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem LF320 LLDPE Cast Film Extrusion Polyethylene Copolymer LF320 is a linear low-density polyethylene, copolymer of butene-1, produced by the gas phase process. It was developed for cast film extrusion. Films obtained with this product show a good processin..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem PB681 LDPE Cast and Blown Film Extrusion, Injection Molding Polyethylene PB681 is a resin produced under high pressure in a tubular reactor. This resin presents excellent 'draw down' (stability to form fine films). The films produced with this resin have excellent optica..
Film Tensile Strength at Break, TD	20.0 MPa @Thickness 0.0381 mm	2900 psi @Thickness 0.00150 in	ASTM D-882
Bapolene® 107A Low Density Polyethylene Film Extrusion Resin Bapolene® 107A is an LDPE for blown film. It contains 3400 ppm antiblock additive. This product meets the Food and Drug Administration requirements of 21CFR177.1520.Applications: General purpose p..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
Braskem BF2021 Cast Film Extrusion Low Density Polyethylene Films for diapers and absorbent articles; Medium resistance films or for general use.Information provided by Braskem.
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM-D882
Braskem LF218/21 LLDPE Cast and Blown Film Extrusion Polyethylene Copolymer LF218/21 is a LLDPE Butene copolymer produced by Braskem. It was specially designed to provide outstanding processing performance. Films obtained with this grade show good physical and optical prope..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
M. Holland Company LL106 LLDPE (discontinued **) Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Hexane Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2..
Film Tensile Strength at Break, TD	20.0 - 58.0 MPa	2900 - 8410 psi	Average value: 34.8 MPa Grade Count:80
Overview of materials for Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade". Each property range of values reported is m..
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
ExxonMobil Escorene® LD-316 EVA Film Resin, High Clarity, High Impact (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 1.9% vinyl acetate copolymer, high clarity film resin. Film made from LD-316 offers improved impact strength and heat sealability versus homopoly..